- 密度 [g/cm3]: 1.01
- 吸水率 [%]: 1.0
- 热变形温度 [℃]: 55.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.01 g/cc | 0.0365 lb/in³ | ISO 1183 |
| Water Absorption at Saturation | 1.0 % | 1.0 % | ISO 62 |
| Viscosity Test | 190 cm³/g | 190 cm³/g | Viscosity Number; ISO 307 |
| Linear Mold Shrinkage | 0.0060 - 0.0090 cm/cm @Thickness 3.00 mm | 0.0060 - 0.0090 in/in @Thickness 0.118 in | sheet with film gate at rim, mold temperature 80°C |
| Linear Mold Shrinkage, Transverse | 0.0070 - 0.013 cm/cm @Thickness 3.00 mm | 0.0070 - 0.013 in/in @Thickness 0.118 in | sheet with film gate at rim, mold temperature 80°C |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 40 | 40 | ISO 868 |
| Tensile Strength at Break | 17.0 MPa | 2470 psi | ISO 527-1, ISO 527-2 |
| Elongation at Break | >= 200 % | >= 200 % | ISO 527-1, ISO 527-2 |
| Tensile Modulus | 0.0800 GPa | 11.6 ksi | ISO 527-1, ISO 527-2 |
| 50% Modulus | 0.00950 GPa | 1.38 ksi | ISO 527-1, ISO 527-2 |
| Charpy Impact Unnotched | NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ISO 179/1eU |
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | ISO 179/1eU | |
| Charpy Impact, Notched | NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ISO 179/1eA |
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | ISO 179/1eA | |
| Tensile Creep Modulus, 1000 hours | 60.0 MPa | 8700 psi | ISO 899-1 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+11 ohm-cm | 1.00e+11 ohm-cm | Spec.; IEC 60093 |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | Spec.; IEC 60093 |
| Dielectric Constant | 4.9 @Frequency 1e+6 Hz | 4.9 @Frequency 1e+6 Hz | IEC 60250 |
| 7.5 @Frequency 100 Hz | 7.5 @Frequency 100 Hz | IEC 60250 | |
| Dielectric Strength | 35.0 kV/mm | 889 kV/in | K20/P50; IEC 60243-1 |
| Dissipation Factor | 0.070 @Frequency 100 Hz | 0.070 @Frequency 100 Hz | IEC 60250 |
| 0.12 @Frequency 1e+6 Hz | 0.12 @Frequency 1e+6 Hz | IEC 60250 | |
| Comparative Tracking Index | 600 V | 600 V | Test Solution A; IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 240 µm/m-°C @Temperature 23.0 - 55.0 °C | 133 µin/in-°F @Temperature 73.4 - 131 °F | Longitudinal; ISO 11359 |
| CTE, linear, Transverse to Flow | 210 µm/m-°C @Temperature 23.0 - 55.0 °C | 117 µin/in-°F @Temperature 73.4 - 131 °F | ISO 11359 |
| Deflection Temperature at 0.46 MPa (66 psi) | 55.0 °C | 131 °F | ISO 75-2 |
| Vicat Softening Point | 60.0 °C | 140 °F | 50N; ISO 306 |
| 125 °C | 257 °F | 10N; ISO 306 | |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |