- 弯曲模量 [MPa]: 7.50
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.65 g/cc | 1.65 g/cc | ISO 1183 | ||
| Water Absorption | <= 0.10 % | <= 0.10 % | 23°C/24h | ||
| Linear Mold Shrinkage | 0.0020 - 0.0050 cm/cm | 0.0020 - 0.0050 in/in | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Stress | 105 MPa | 15200 psi | |||
| Elongation at Yield | 3.0 % | 3.0 % | |||
| 3.8 % | 3.8 % | flexural | |||
| Modulus of Elasticity | 8.60 GPa | 1250 ksi | |||
| Flexural Strength | 165 MPa | 23900 psi | |||
| Flexural Modulus | 7.50 GPa | 1090 ksi | |||
| Charpy Impact Unnotched | 4.80 J/cm² | 22.8 ft-lb/in² | edgewise; ISO 179 1eU | ||
| Electrical Properties | Metric | English | Comments | ||
| Surface Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm | |||
| Insulation Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm | |||
| Thermal Properties | Metric | English | Comments | ||
| Thermal Conductivity | 1.50 W/m-K | 10.4 BTU-in/hr-ft²-°F | HOT-DISK || 60x60x3 mm | ||
| Maximum Service Temperature, Air | 90.0 °C | 194 °F | |||
| 140 °C | 284 °F | short term | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 250 °C | 482 °F | mass temp | ||
| Nozzle Temperature | 250 - 260 °C | 482 - 500 °F | |||
| Zone 1 | 230 - 250 °C | 446 - 482 °F | |||
| Zone 2 | 240 - 260 °C | 464 - 500 °F | |||
| Zone 3 | 250 - 270 °C | 482 - 518 °F | |||
| Mold Temperature | 70.0 - 110 °C | 158 - 230 °F | |||
| Drying Temperature | 75.0 °C @Time 21600 - 36000 sec | 167 °F @Time 6.00 - 10.0 hour | Dehumidifying dryer | ||
| 105 °C @Time <=14400 sec | 221 °F @Time <=4.00 hour | or | |||
| Descriptive Properties | |||||
| Color | graphite grey | ||||