- 密度 [g/cm3]: 1.19
- 缺口冲击强度: 1.27
- 拉伸强度 [MPa]: 92.0
- 弯曲模量 [MPa]: 4.48
- 热变形温度 [℃]: 170.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Density | 1.19 g/cc | 0.0430 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.150 % | 0.150 % | 50% RH, 24 hrs; ASTM D570 |
| 0.200 % | 0.200 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0060 cm/cm @Time 86400 sec | 0.0030 - 0.0060 in/in @Time 24.0 hour | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0090 - 0.020 cm/cm @Time 86400 sec | 0.0090 - 0.020 in/in @Time 24.0 hour | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 86.0 MPa | 12500 psi | Type I, 5 mm/min; ASTM D638 |
| 91.0 MPa | 13200 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 92.0 MPa | 13300 psi | 5 mm/min; ISO 527 |
| 93.0 MPa | 13500 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 6.1 % | 6.1 % | Type I, 5 mm/min; ASTM D638 |
| 6.3 % | 6.3 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 4.9 % | 4.9 % | Type I, 5 mm/min; ASTM D638 |
| 4.9 % | 4.9 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 5.41 GPa | 785 ksi | 50 mm/min; ASTM D638 |
| 5.41 GPa | 785 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 136 MPa | 19700 psi | ISO 178 |
| Flexural Modulus | 4.48 GPa | 650 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 4.72 GPa | 685 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 1.27 J/cm | 2.38 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 8.70 J/cm | 16.3 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 58.0 kJ/m² | 27.6 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 16.0 J @Temperature 23.0 °C | 11.8 ft-lb @Temperature 73.4 °F | ASTM D3763 |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.48 | 0.48 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.47 | 0.47 | ASTM D3702 Modified |
| K (wear) Factor | 14.1 x 10-8 mm³/N-M | 7.00 x 10-10 in³-min/ft-lb-hr | Ring; ASTM D3702 Modified |
| 103 x 10-8 mm³/N-M | 51.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 40.0 µm/m-°C @Temperature -30.0 - 30.0 °C | 22.2 µin/in-°F @Temperature -22.0 - 86.0 °F | ASTM D696 |
| CTE, linear, Transverse to Flow | 13.5 µm/m-°C @Temperature -30.0 - 30.0 °C | 7.50 µin/in-°F @Temperature -22.0 - 86.0 °F | ASTM D696 |
| 1350 µm/m-°C @Temperature -30.0 - 30.0 °C | 750 µin/in-°F @Temperature -22.0 - 86.0 °F | ASTM D696 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 170 °C | 338 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 175 °C @Thickness 3.20 mm | 347 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 146 °C | 295 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 161 °C @Thickness 3.20 mm | 322 °F @Thickness 0.126 in | unannealed; ASTM D648 | |