- 熔体流动速率 [g/10min]: 8.8
- 密度 [g/cm3]: 1.03
- 拉伸强度 [MPa]: 40.0
- 热变形温度 [℃]: 145.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.03 g/cc | 0.0372 lb/in³ | |
| Melt Flow | 8.8 g/10 min @Load 2.16 kg, Temperature 235 °C | 8.8 g/10 min @Load 4.76 lb, Temperature 455 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 40.0 MPa | 5800 psi | 50 mm/min |
| Elongation at Break | >= 50 % | >= 50 % | Nominal Strain; 50 mm/min |
| Elongation at Yield | 5.0 % | 5.0 % | 50 mm/min |
| Tensile Modulus | 1.42 GPa | 206 ksi | 1 mm/min |
| Charpy Impact Unnotched | NB | NB | |
| NB | NB | Low Temp | |
| Charpy Impact, Notched | 1.15 J/cm² | 5.47 ft-lb/in² | |
| 1.38 J/cm² @Temperature -30.0 °C | 6.57 ft-lb/in² @Temperature -22.0 °F | ||
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 145 °C | 293 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | |
| Vicat Softening Point | 160 °C | 320 °F | 50°C/hr; 50N |