- 密度 [g/cm3]: 1.24
- 缺口冲击强度: 0.85
- 拉伸强度 [MPa]: 45.0
- 弯曲模量 [MPa]: 1.92
- 热变形温度 [℃]: 151.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.24 g/cc | 0.0448 lb/in³ | ISO 1183 |
| 1.27 g/cc | 0.0459 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.100 % | 0.100 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.017 cm/cm @Time 86400 sec | 0.017 in/in @Time 24.0 hour | ASTM D955 |
| 0.017 cm/cm @Time 86400 sec | 0.017 in/in @Time 24.0 hour | ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.015 cm/cm @Time 86400 sec | 0.015 in/in @Time 24.0 hour | ASTM D955 |
| 0.015 cm/cm @Time 86400 sec | 0.015 in/in @Time 24.0 hour | ISO 294 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 41.0 MPa | 5950 psi | ISO 527 |
| 43.0 MPa | 6240 psi | ASTM D638 | |
| Tensile Strength, Yield | 45.0 MPa | 6530 psi | ASTM D638 |
| 46.0 MPa | 6670 psi | ISO 527 | |
| Elongation at Break | 20 % | 20 % | ASTM D638 |
| 43.2 % | 43.2 % | ISO 527 | |
| Elongation at Yield | 23.2 % | 23.2 % | ASTM D638 |
| 23.7 % | 23.7 % | ISO 527 | |
| Tensile Modulus | 1.96 GPa | 284 ksi | 50 mm/min; ASTM D638 |
| 2.09 GPa | 303 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 55.0 MPa | 7980 psi | ASTM D790 |
| 58.0 MPa | 8410 psi | ISO 178 | |
| Flexural Modulus | 1.92 GPa | 278 ksi | ASTM D790 |
| 3.00 GPa | 435 ksi | ISO 178 | |
| Izod Impact, Notched | 0.850 J/cm | 1.59 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 15.48 J/cm | 29.00 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 165 kJ/m² | 78.5 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 33.0 J | 24.3 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 151 °C | 304 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 145 °C @Thickness 3.20 mm | 293 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 47.0 °C | 117 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 46.0 °C @Thickness 3.20 mm | 115 °F @Thickness 0.126 in | unannealed; ASTM D648 | |