- 密度 [g/cm3]: 1.42
- 吸水率 [%]: 0.14
- 缺口冲击强度: 1.6
- 弯曲模量 [MPa]: 8.62
- 硬度: 118.0
- 热变形温度 [℃]: 215.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.42 g/cc | 1.42 g/cc | DAM; ASTM D792 | ||
| Density | 1.42 g/cc | 0.0513 lb/in³ | DAM; ISO 1183 | ||
| Filler Content | 43 % | 43 % | DAM | ||
| Water Absorption | 0.14 % @Temperature 23.0 °C | 0.14 % @Temperature 73.4 °F | Immersion 24h; DAM; ASTM D570 | ||
| 1.7 % @Temperature 23.0 °C | 1.7 % @Temperature 73.4 °F | Saturation, immersed; DAM; ISO 62, Similar to | |||
| 1.7 % @Thickness 2.00 mm, Temperature 23.0 °C | 1.7 % @Thickness 0.0787 in, Temperature 73.4 °F | Saturation; DAM; ASTM D570 | |||
| 2.1 % @Thickness 1.00 mm, Temperature 23.0 °C | 2.1 % @Thickness 0.0394 in, Temperature 73.4 °F | Equilibrium 50%RH; DAM; ISO 62, Similar to | |||
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm @Thickness 2.00 mm | 0.0030 in/in @Thickness 0.0787 in | Parallel; DAM; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm @Thickness 2.00 mm | 0.0080 in/in @Thickness 0.0787 in | Normal; DAM; ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 118 | 118 | DAM; ISO 2039/2 | ||
| 118 | 118 | DAM; ASTM D785 | |||
| Tensile Strength at Break | 165 MPa @Temperature 23.0 °C | 23900 psi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 200 MPa @Temperature 23.0 °C | 29000 psi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Tensile Strength | 165 MPa @Temperature 23.0 °C | 23900 psi @Temperature 73.4 °F | 50%RH; ASTM D638 | ||
| 190 MPa @Temperature 23.0 °C | 27600 psi @Temperature 73.4 °F | DAM; ASTM D638 | |||
| Elongation at Break | 3.0 % @Temperature 23.0 °C | 3.0 % @Temperature 73.4 °F | DAM; ASTM D638 | ||
| 3.0 % @Temperature 23.0 °C | 3.0 % @Temperature 73.4 °F | DAM; ISO 527 | |||
| 5.0 % @Temperature 23.0 °C | 5.0 % @Temperature 73.4 °F | 50%RH; ASTM D638 | |||
| 5.0 % @Temperature 23.0 °C | 5.0 % @Temperature 73.4 °F | 50%RH; ISO 527 | |||
| Tensile Modulus | 11.5 GPa @Temperature 23.0 °C | 1670 ksi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 12.5 GPa @Temperature 23.0 °C | 1810 ksi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Flexural Strength | 269 MPa @Temperature 23.0 °C | 39000 psi @Temperature 73.4 °F | DAM; ASTM D790 | ||
| Flexural Modulus | 8.62 GPa @Temperature 23.0 °C | 1250 ksi @Temperature 73.4 °F | 50%RH; ASTM D790 | ||
| 11.0 GPa @Temperature 23.0 °C | 1600 ksi @Temperature 73.4 °F | DAM; ISO 178 | |||
| 11.0 GPa @Temperature 23.0 °C | 1600 ksi @Temperature 73.4 °F | DAM; ASTM D790 | |||
| Shear Strength | 83.0 MPa @Temperature 23.0 °C | 12000 psi @Temperature 73.4 °F | DAM; ASTM D732 | ||
| Izod Impact, Notched | 1.60 J/cm @Temperature 23.0 °C | 3.00 ft-lb/in @Temperature 73.4 °F | 50%RH; ASTM D256 | ||
| 1.70 J/cm @Temperature 23.0 °C | 3.18 ft-lb/in @Temperature 73.4 °F | DAM; ASTM D256 | |||
| Izod Impact, Notched (ISO) | 15.0 kJ/m² @Temperature -40.0 °C | 7.14 ft-lb/in² @Temperature -40.0 °F | DAM; ISO 180/1A | ||
| 17.0 kJ/m² @Temperature 23.0 °C | 8.09 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 180/1A | |||
| Charpy Impact Unnotched | 8.50 J/cm² @Temperature -30.0 °C | 40.4 ft-lb/in² @Temperature -22.0 °F | DAM; ISO 179/1eU | ||
| 10.0 J/cm² @Temperature 23.0 °C | 47.6 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 179/1eU | |||
| Charpy Impact, Notched | 1.70 J/cm² @Temperature -40.0 °C | 8.09 ft-lb/in² @Temperature -40.0 °F | DAM; ISO 179/1eA | ||
| 1.70 J/cm² @Temperature -30.0 °C | 8.09 ft-lb/in² @Temperature -22.0 °F | DAM; ISO 179/1eA | |||
| 1.70 J/cm² @Temperature 23.0 °C | 8.09 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+12 ohm-cm @Temperature 23.0 °C | 1.00e+12 ohm-cm @Temperature 73.4 °F | 50%RH; ASTM D257 | ||
| 1.00e+15 ohm-cm @Temperature 23.0 °C | 1.00e+15 ohm-cm @Temperature 73.4 °F | DAM; ASTM D257 | |||
| 1.00e+15 ohm-cm @Temperature 23.0 °C | 1.00e+15 ohm-cm @Temperature 73.4 °F | DAM; IEC 60093 | |||
| Surface Resistance | 1.00e+15 ohm @Temperature 23.0 °C | 1.00e+15 ohm @Temperature 73.4 °F | DAM; ASTM D257 | ||
| Dielectric Constant | 3.6 @Frequency 1.00e+6 Hz, Temperature 23.0 °C | 3.6 @Frequency 1.00e+6 Hz, Temperature 73.4 °F | DAM; ASTM D150 | ||
| 3.6 @Frequency 1.00e+6 Hz, Temperature 23.0 °C | 3.6 @Frequency 1.00e+6 Hz, Temperature 73.4 °F | DAM; IEC 60250 | |||
| 4.0 @Frequency 1000 Hz, Temperature 23.0 °C | 4.0 @Frequency 1000 Hz, Temperature 73.4 °F | DAM; ASTM D150 | |||
| Dielectric Strength | 19.7 kV/mm @Thickness 3.20 mm, Temperature 23.0 °C | 500 kV/in @Thickness 0.126 in, Temperature 73.4 °F | DAM; Short Time; ASTM D149 | ||
| Dissipation Factor | 0.020 @Frequency 1.00e+6 Hz, Temperature 23.0 °C | 0.020 @Frequency 1.00e+6 Hz, Temperature 73.4 °F | DAM; ASTM D150 | ||
| 0.020 @Frequency 1.00e+6 Hz, Temperature 23.0 °C | 0.020 @Frequency 1.00e+6 Hz, Temperature 73.4 °F | DAM; IEC 60250 | |||
| 0.030 @Frequency 1000 Hz, Temperature 23.0 °C | 0.030 @Frequency 1000 Hz, Temperature 73.4 °F | DAM; ASTM D150 | |||
| Comparative Tracking Index | >= 600 V @Thickness 3.00 mm, Temperature 23.0 °C | >= 600 V @Thickness 0.118 in, Temperature 73.4 °F | DAM; UL 746A | ||
| >= 600 V @Thickness 3.00 mm, Temperature 23.0 °C | >= 600 V @Thickness 0.118 in, Temperature 73.4 °F | DAM; UL 746A | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 500 µm/m-°C @Temperature -40.0 - 23.0 °C | 278 µin/in-°F @Temperature -40.0 - 73.4 °F | DAM; ASTM E 831 | ||
| 500 µm/m-°C @Temperature 23.0 - 55.0 °C | 278 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ASTM E 831 | |||
| 500 µm/m-°C @Temperature 55.0 - 160 °C | 278 µin/in-°F @Temperature 131 - 320 °F | DAM; ASTM E 831 | |||
| 500 µm/m-°C @Temperature -40.0 - 23.0 °C | 278 µin/in-°F @Temperature -40.0 - 73.4 °F | DAM; ISO 11359-1/-2 | |||
| 500 µm/m-°C @Temperature 23.0 - 55.0 °C | 278 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 | |||
| 500 µm/m-°C @Temperature 55.0 - 160 °C | 278 µin/in-°F @Temperature 131 - 320 °F | DAM; ISO 11359-1/-2 | |||
| CTE, linear, Transverse to Flow | 73.0 µm/m-°C @Temperature -40.0 - 23.0 °C | 40.6 µin/in-°F @Temperature -40.0 - 73.4 °F | DAM; ASTM E 831 | ||
| 73.0 µm/m-°C @Temperature -40.0 - 23.0 °C | 40.6 µin/in-°F @Temperature -40.0 - 73.4 °F | DAM; ISO 11359-1/-2 | |||
| 104 µm/m-°C @Temperature 23.0 - 55.0 °C | 57.8 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ASTM E 831 | |||
| 104 µm/m-°C @Temperature 23.0 - 55.0 °C | 57.8 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 | |||
| 139 µm/m-°C @Temperature 55.0 - 160 °C | 77.2 µin/in-°F @Temperature 131 - 320 °F | DAM; ASTM E 831 | |||
| 139 µm/m-°C @Temperature 55.0 - 160 °C | 77.2 µin/in-°F @Temperature 131 - 320 °F | DAM; ISO 11359-1/-2 | |||
| Melting Point | 217 °C | 423 °F | DAM; ASTM D3418 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | DAM; ASTM D648 | ||
| 217 °C | 423 °F | DAM; ISO 75-1/-2 | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 203 °C | 397 °F | DAM; ISO 75-1/-2 | ||
| 205 °C | 401 °F | DAM; ASTM D648 | |||
| Glass Transition Temp, Tg | 70.0 °C | 158 °F | 10°C/min; DAM; ISO 11357-1/-2 | ||
| UL RTI, Electrical | 105 °C @Thickness 0.710 mm | 221 °F @Thickness 0.0280 in | DAM; UL 746B | ||
| 120 °C @Thickness 3.00 mm | 248 °F @Thickness 0.118 in | DAM; UL 746B | |||
| 120 °C @Thickness 1.50 mm | 248 °F @Thickness 0.0591 in | DAM; UL 746B | |||
| UL RTI, Mechanical without Impact | 120 °C @Thickness 1.50 mm | 248 °F @Thickness 0.0591 in | DAM; UL 746B | ||
| 120 °C @Thickness 3.00 mm | 248 °F @Thickness 0.118 in | DAM; UL 746B | |||
| Flammability, UL94 | HB @Thickness 0.710 mm | HB @Thickness 0.0280 in | DAM; UL94 | ||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | DAM; UL94 | |||
| HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | DAM; UL94 | |||
| HB @Thickness 0.710 mm | HB @Thickness 0.0280 in | DAM; IEC 60695-11-10 | |||
| HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | DAM; IEC 60695-11-10 | |||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | DAM; IEC 60695-11-10 | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 218 °C | 424 °F | 10°C/min; DAM; ISO 11357-1/-3 | ||
| 280 - 300 °C | 536 - 572 °F | DAM | |||
| 290 °C | 554 °F | DAM; Optimum | |||
| Mold Temperature | 70.0 - 120 °C | 158 - 248 °F | DAM | ||
| 100 °C | 212 °F | DAM; optimum | |||
| Drying Temperature | 80.0 °C | 176 °F | DAM | ||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM | ||
| Moisture Content | <= 0.15 % | <= 0.15 % | DAM | ||
| Descriptive Properties | |||||
| Additive | Lubricant | DAM | |||
| Appearance | Natural Color | DAM | |||
| Drying Recommended | Yes, if moisture content of resin exceeds recommended level | DAM | |||
| Features | Dimensional Stability, Good | DAM | |||
| Lubricated | DAM | ||||
| Moisture Absorption, Low | DAM | ||||
| Filler | Glass fiber reinforcement | DAM | |||
| Forms | Pellets | DAM | |||
| Generic | Nylon 612 | DAM | |||
| Material Status | Current | DAM | |||
| Part Marking Code | >PA612-GF43< | ISO 11469; DAM | |||
| Polymer Family | Polyamide | DAM | |||
| Polymer Type | PA612 | DAM | |||
| Processing Method | Injection Molding | DAM | |||
| Product Category | Glass Reinforced Resins | DAM | |||
| Region Available - Global | Yes | DAM | |||
| Resin Identification | PA612-GF43 | ISO 1043; DAM | |||
| RoHS Compliance | Contact Manufacturer | DAM | |||
| Ultrasonic Weldable | Yes | DAM | |||
| Uses | Appliance Components | DAM | |||
| Automotive Applications | DAM | ||||
| Electrical/Electronic Applications | DAM | ||||
| Industrial Applications | DAM | ||||