- 吸水率 [%]: 0.2
- 缺口冲击强度: 1.2
- 弯曲模量 [MPa]: 10.3
- 热变形温度 [℃]: 210.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.43 g/cc | 1.43 g/cc | ASTM D792 | ||
| Water Absorption | 0.20 % @Thickness 3.18 mm | 0.20 % @Thickness 0.125 in | @ 24 hrs; ASTM D570 | ||
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm | 0.0020 in/in | ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 167 MPa | 24200 psi | Type I, 5.1 mm/min; ASTM D638 | ||
| Elongation at Break | 3.5 % | 3.5 % | Type I, 5.1 mm/min; ASTM D638 | ||
| Flexural Strength | 255 MPa | 37000 psi | ASTM D790 | ||
| Flexural Modulus | 10.3 GPa | 1490 ksi | ASTM D790 | ||
| Izod Impact, Notched | 1.20 J/cm @Thickness 3.18 mm, Temperature 23.0 °C | 2.25 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F | Injection Molded; ASTM D256A | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 215 °C | 419 °F | ASTM D789 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C @Thickness 3.18 mm | 410 °F @Thickness 0.125 in | Unannealed; ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C @Thickness 3.18 mm | 392 °F @Thickness 0.125 in | Unannealed; ASTM D648 | ||
| Processing Properties | Metric | English | Comments | ||
| Mold Temperature | 48.9 - 93.3 °C | 120 - 200 °F | |||
| Drying Temperature | 82.2 °C | 180 °F | |||
| Dry Time | 4.00 hour | 4.00 hour | |||
| Descriptive Properties | |||||
| Appearance | Black | ||||
| Filler / Reinforcement | Glass Fiber Reinforcement | ||||
| Unspecified Filler\Reinfor., 43% Filler by Weight | |||||
| Forms | Pellets | ||||
| Generic Material | Nylon 612 | ||||
| Generic Name | Polyamide 612 (Nylon 612) | ||||
| Regional Availability | North America | ||||
| South America | |||||