- 吸水率 [%]: 0.3
- 缺口冲击强度: 0.43
- 弯曲模量 [MPa]: 3.45
- 热变形温度 [℃]: 200.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.13 g/cc | 1.13 g/cc | ASTM D792 | ||
| Water Absorption | 0.30 % | 0.30 % | @ 24 hrs; ASTM D570 | ||
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0060 cm/cm @Thickness 3.18 mm | 0.0050 - 0.0060 in/in @Thickness 0.125 in | ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 82.7 MPa | 12000 psi | 5.1 mm/min; ASTM D638 | ||
| Elongation at Break | 5.0 % | 5.0 % | ASTM D638 | ||
| Tensile Modulus | 4.14 GPa | 600 ksi | 5.1 mm/min; ASTM D638 | ||
| Flexural Strength | 131 MPa | 19000 psi | 1.3 mm/min; ASTM D790 | ||
| Flexural Modulus | 3.45 GPa | 500 ksi | 1.3 mm/min; ASTM D790 | ||
| Izod Impact, Notched | 0.430 J/cm | 0.806 ft-lb/in | Injection Molded; ASTM D256A | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 200 °C | 392 °F | Unannealed; ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 175 °C | 347 °F | Unannealed; ASTM D648 | ||
| Descriptive Properties | |||||
| Features | Good Chemical Resistance | ||||
| Good Stability | |||||
| Low to No Water Absorption | |||||
| Semi Crystalline | |||||
| Filler / Reinforcement | Glass Fiber Reinforcement, 10% Filler by Weight | ||||
| Forms | Pellets | ||||
| Generic Material | Nylon 612 | ||||
| Generic Name | Polyamide 612 (Nylon 612) | ||||
| Regional Availability | Africa & Middle East | ||||
| Asia Pacific | |||||
| Europe | |||||
| North America | |||||
| South America | |||||
| RoHS Compliance | RoHS Compliant | ||||
| Uses | Aerospace Applications | ||||
| Appliance Components | |||||
| Appliances | |||||
| Automotive Applications | |||||
| Electrical/Electronic Applications | |||||
| Housings | |||||
| Industrial Applications | |||||
| Marine Applications | |||||
| Sporting Goods | |||||