- 密度 [g/cm3]: 1.19
- 吸水率 [%]: 2.0
- 热变形温度 [℃]: 208.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.80 % | 0.80 % | 23°C/50% R.H.; ISO 62 |
| Water Absorption at Saturation | 2.0 % | 2.0 % | ISO 62 |
| Linear Mold Shrinkage | 0.0066 cm/cm | 0.0066 in/in | 127x12.7x3.2 mm (processing cond. acc. To DIN EN ISO 1874-2) |
| Linear Mold Shrinkage, Transverse | 0.0088 cm/cm | 0.0088 in/in | 127x12.7x3.2 mm (processing cond. acc. To DIN EN ISO 1874-2) |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 109 MPa | 15800 psi | ISO 527-2/1A |
| Elongation at Break | 6.0 % | 6.0 % | ISO 527-2/1A |
| Tensile Modulus | 5.45 GPa | 790 ksi | ISO 527-2/1A |
| Charpy Impact Unnotched | 9.30 J/cm² @Temperature 23.0 °C | 44.3 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU |
| 10.6 J/cm² @Temperature -30.0 °C | 50.4 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eU | |
| Charpy Impact, Notched | 1.10 J/cm² @Temperature -30.0 °C | 5.24 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA |
| 1.80 J/cm² @Temperature 23.0 °C | 8.57 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | IEC 60093 |
| Dielectric Constant | 3.1 @Frequency 1e+6 Hz | 3.1 @Frequency 1e+6 Hz | IEC 60250 |
| 4.4 @Frequency 100 Hz | 4.4 @Frequency 100 Hz | IEC 60250 | |
| Dissipation Factor | 0.047 @Frequency 1e+6 Hz | 0.047 @Frequency 1e+6 Hz | IEC 60250 |
| 0.050 @Frequency 100 Hz | 0.050 @Frequency 100 Hz | IEC 60250 | |
| Comparative Tracking Index | >= 600 V | >= 600 V | Test Solution A, 50 drops; IEC 60112 |
| 600 V | 600 V | Test Solution A, 100 drops; IEC 60112 | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 50.0 µm/m-°C @Temperature 23.0 - 55.0 °C | 27.8 µin/in-°F @Temperature 73.4 - 131 °F | Longitudinal; ISO 11359 |
| CTE, linear, Transverse to Flow | 70.0 µm/m-°C @Temperature 23.0 - 55.0 °C | 38.9 µin/in-°F @Temperature 73.4 - 131 °F | ISO 11359 |
| Melting Point | 215 °C | 419 °F | Peak Temperature; ISO 11357 |
| Deflection Temperature at 0.46 MPa (66 psi) | 208 °C | 406 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 189 °C | 372 °F | ISO 75 |
| Vicat Softening Point | 207 °C | 405 °F | 50N; ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |