- 密度 [g/cm3]: 1.08
- 吸水率 [%]: 1.7
- 拉伸强度 [MPa]: 70.0
- 热变形温度 [℃]: 150.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.08 g/cc @Temperature 23.0 °C | 0.0390 lb/in³ @Temperature 73.4 °F | ISO 1183 | ||
| Water Absorption | 1.7 % @Temperature 23.0 °C | 1.7 % @Temperature 73.4 °F | 50% r.h.; ISO 62 | ||
| Spiral Flow | 700 cm | 276 in | AKRO | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 70.0 MPa | 10200 psi | 5 [mm/min], Test Speed 50 [mm/min]; ISO 527-1/2 | ||
| Elongation at Break | >= 50 % | >= 50 % | 5 [mm/min]; ISO 527-1/2 | ||
| Tensile Modulus | 2.40 GPa | 348 ksi | 1[mm/min]; ISO 527-1/2 | ||
| Charpy Impact Unnotched | NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | ISO 179/1eU | ||
| NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 0.400 J/cm² @Temperature 23.0 °C | 1.90 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | ||
| 0.400 J/cm² @Temperature -30.0 °C | 1.90 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 220 °C | 428 °F | ISO 11357-1, DSC,10 [K/min] | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 150 °C | 302 °F | HDT/B; ISO 75-1/2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | HDT/A; ISO 75-1/2 | ||
| Flammability, UL94 | HB @Thickness 0.800 mm | HB @Thickness 0.0315 in | |||
| Processing Properties | Metric | English | Comments | ||
| Feed Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |||
| Nozzle Temperature | 240 - 295 °C | 464 - 563 °F | |||
| Zone 1 | 225 - 300 °C | 437 - 572 °F | |||
| Zone 2 | 225 - 300 °C | 437 - 572 °F | |||
| Zone 3 | 225 - 300 °C | 437 - 572 °F | |||
| Zone 4 | 225 - 300 °C | 437 - 572 °F | |||
| Melt Temperature | 260 - 320 °C | 500 - 608 °F | |||
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | |||
| Drying Temperature | 80.0 °C | 176 °F | |||
| Dry Time | 2 - 8 hour | 2 - 8 hour | |||
| Injection Pressure | 100 MPa | 14500 psi | |||
| Hold Pressure | 75.0 MPa | 10900 psi | |||
| Back Pressure | 0.400 - 1.00 MPa | 58.0 - 145 psi | |||
| Descriptive Properties | |||||
| Rate acc. FMVSS 302 (<100/min) | Passed | ||||
| Rate acc. FMVSS 302,(<100/min) | FMVSS 302, >1 [mm] Thickness | ||||