- 缺口冲击强度: 0.53
- 弯曲模量 [MPa]: 4.14
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.14 g/cc | 1.14 g/cc | ASTM D792 | ||
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm | 0.0040 in/in | ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 82.7 MPa | 12000 psi | Type I, 5.1 mm/min; ASTM D638 | ||
| Elongation at Break | 4.0 % | 4.0 % | Type I, 5.1 mm/min; ASTM D638 | ||
| Flexural Strength | 124 MPa | 18000 psi | ASTM D790 | ||
| Flexural Modulus | 4.14 GPa | 600 ksi | ASTM D790 | ||
| Izod Impact, Notched | 0.530 J/cm @Thickness 6.35 mm, Temperature 23.0 °C | 0.993 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F | Injection Molded; ASTM D256A | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 282 °C | 540 °F | |||
| Mold Temperature | 93.3 °C | 200 °F | |||
| Drying Temperature | 93.3 °C | 200 °F | |||
| Dry Time | 4.00 hour | 4.00 hour | |||
| Descriptive Properties | |||||
| Filler / Reinforcement | Glass Fiber Reinforcement | ||||
| Forms | Pellets | ||||
| Generic Material | Nylon 610 | ||||
| Generic Name | Polyamide 610 (Nylon 610) | ||||
| Regional Availability | Africa & Middle East | ||||
| Asia Pacific | |||||
| Europe | |||||
| North America | |||||
| South America | |||||