- 密度 [g/cm3]: 1.3
- 弯曲模量 [MPa]: 8.00
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in³ | ISO 1183/A | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 152 MPa | 22000 psi | ISO 527 Type 1A | ||
| Elongation at Break | 4.4 % | 4.4 % | ISO 527 Type 1A | ||
| Tensile Modulus | 8.50 GPa | 1230 ksi | ISO 527 Type 1A | ||
| Flexural Strength | 250 MPa | 36300 psi | ISO 178 | ||
| Flexural Modulus | 8.00 GPa | 1160 ksi | ISO 178 | ||
| Charpy Impact Unnotched | 8.50 J/cm² @Temperature -30.0 °C | 40.4 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eU | ||
| 9.00 J/cm² @Temperature 23.0 °C | 42.8 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 1.00 J/cm² @Temperature -30.0 °C | 4.76 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA | ||
| 1.40 J/cm² @Temperature 23.0 °C | 6.66 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 195 °C | 383 °F | ISO 75/Af | ||
| Flammability, UL94 | HB @Thickness 0.800 mm | HB @Thickness 0.0315 in | ISO 1210 | ||
| HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | ISO 1210 | |||
| HB @Thickness 3.20 mm | HB @Thickness 0.126 in | ISO 1210 | |||
| Processing Properties | Metric | English | Comments | ||
| Feed Temperature | 225 - 230 °C | 437 - 446 °F | |||
| Melt Temperature | 215 °C | 419 °F | ISO 11357 | ||
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | |||
| Drying Temperature | 80.0 °C | 176 °F | |||
| Moisture Content | <= 0.20 % | <= 0.20 % | |||
| Descriptive Properties | |||||
| Compression Zone | 230-240°C | ||||
| Mixing Zone | 240-250°C | ||||