- 密度 [g/cm3]: 1.52
- 缺口冲击强度: 0.53
- 拉伸强度 [MPa]: 162.0
- 弯曲模量 [MPa]: 13.0
- 热变形温度 [℃]: 218.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.52 g/cc | 0.0549 lb/in³ | ASTM D792 |
| 1.52 g/cc | 0.0549 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.100 % | 0.100 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm @Time 86400 sec | 0.0010 in/in @Time 24.0 hour | ASTM D955 |
| 0.0011 cm/cm @Time 86400 sec | 0.0011 in/in @Time 24.0 hour | ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0078 cm/cm @Time 86400 sec | 0.0078 in/in @Time 24.0 hour | ISO 294 |
| 0.0080 cm/cm @Time 86400 sec | 0.0080 in/in @Time 24.0 hour | ASTM D955 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 158 MPa | 22900 psi | ASTM D638 |
| 162 MPa | 23500 psi | ISO 527 | |
| Tensile Strength, Yield | 162 MPa | 23500 psi | ISO 527 |
| 168 MPa | 24400 psi | ASTM D638 | |
| Elongation at Break | 1.6 % | 1.6 % | ISO 527 |
| 1.9 % | 1.9 % | ASTM D638 | |
| Elongation at Yield | 1.6 % | 1.6 % | ISO 527 |
| 1.8 % | 1.8 % | ASTM D638 | |
| Tensile Modulus | 15.75 GPa | 2284 ksi | 1 mm/min; ISO 527 |
| 16.54 GPa | 2399 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 239 MPa | 34700 psi | ISO 178 |
| 241 MPa | 35000 psi | ASTM D790 | |
| Flexural Modulus | 13.0 GPa | 1890 ksi | ISO 178 |
| 13.1 GPa | 1900 ksi | ASTM D790 | |
| Izod Impact, Notched | 0.530 J/cm | 0.993 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.34 J/cm | 10.0 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 32.0 kJ/m² | 15.2 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 4.00 J | 2.95 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.34 | 0.34 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.28 | 0.28 | ASTM D3702 Modified |
| K (wear) Factor | 894 x 10-8 mm³/N-M | 444 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 55.8 µm/m-°C @Temperature -40.0 - 40.0 °C | 31.0 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 57.0 µm/m-°C @Temperature -40.0 - 40.0 °C | 31.7 µin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 19.0 µm/m-°C @Temperature -40.0 - 40.0 °C | 10.6 µin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 |
| 19.8 µm/m-°C @Temperature -40.0 - 40.0 °C | 11.0 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 218 °C | 424 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 217 °C @Thickness 3.20 mm | 423 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 198 °C | 388 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 200 °C @Thickness 3.20 mm | 392 °F @Thickness 0.126 in | unannealed; ASTM D648 | |