- 密度 [g/cm3]: 1.6
- 缺口冲击强度: 1.6
- 拉伸强度 [MPa]: 181.0
- 断裂伸长率 [%]: 280
- 弯曲模量 [MPa]: 11.44
- 热变形温度 [℃]: 220.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.60 g/cc | 0.0578 lb/in³ | ASTM D792 |
| 1.60 g/cc | 0.0578 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.210 % | 0.210 % | 50% RH, 24 hrs; ASTM D570 |
| 0.280 % | 0.280 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0018 - 0.0020 cm/cm @Time 86400 sec | 0.0018 - 0.0020 in/in @Time 24.0 hour | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.015 cm/cm @Time 86400 sec | 0.0050 - 0.015 in/in @Time 24.0 hour | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 181 MPa | 26300 psi | Type I, 5 mm/min; ASTM D638 |
| 181 MPa | 26300 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 181 MPa | 26300 psi | Type I, 5 mm/min; ASTM D638 |
| 181 MPa | 26300 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 2.3 % | 2.3 % | 5 mm/min; ISO 527 |
| 2.5 % | 2.5 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 2.3 % | 2.3 % | 5 mm/min; ISO 527 |
| 2.5 % | 2.5 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 15.51 GPa | 2250 ksi | 1 mm/min; ISO 527 |
| 18.68 GPa | 2709 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 285 MPa | 41300 psi | brk, 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Yield Strength | 280 MPa | 40600 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 11.44 GPa | 1659 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 12.87 GPa | 1867 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 1.60 J/cm | 3.00 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 13.05 J/cm | 24.45 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 14.0 kJ/m² | 6.66 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 75.0 kJ/m² | 35.7 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 1.50 µm/m-°C @Temperature -40.0 - 40.0 °C | 0.833 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| CTE, linear, Transverse to Flow | 7.83 µm/m-°C @Temperature -40.0 - 40.0 °C | 4.35 µin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 221 °C @Thickness 3.20 mm | 430 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 213 °C @Thickness 3.20 mm | 415 °F @Thickness 0.126 in | unannealed; ASTM D648 | |