- 熔体流动速率 [g/10min]: 5.0
- 吸水率 [%]: 0.2
- 缺口冲击强度: 1.6
- 弯曲模量 [MPa]: 9.17
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.42 g/cc | 1.42 g/cc | ASTM D792 | ||
| Water Absorption | 0.20 % | 0.20 % | 24 hr; ASTM D750 | ||
| Linear Mold Shrinkage | 0.0010 - 0.0030 cm/cm | 0.0010 - 0.0030 in/in | ASTM D955 | ||
| Melt Flow | 5.0 g/10 min | 5.0 g/10 min | at 235°C/1.0 kg; ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength | 165 MPa | 24000 psi | ASTM D638 | ||
| Elongation at Break | 2.7 % | 2.7 % | ASTM D638 | ||
| Elongation at Yield | 2.5 % | 2.5 % | ASTM D638 | ||
| Flexural Strength | 241 MPa | 35000 psi | ASTM D790 | ||
| Flexural Modulus | 9.17 GPa | 1330 ksi | ASTM D790 | ||
| Izod Impact, Notched | 1.60 J/cm @Temperature 22.8 °C | 3.00 ft-lb/in @Temperature 73.0 °F | ASTM D256 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 211 °C | 412 °F | Unannealed; ASTM D648 | ||
| Flammability, UL94 | HB @Thickness 0.810 mm | HB @Thickness 0.0319 in | |||
| Oxygen Index | 25 % | 25 % | ASTM D2863 | ||
| Processing Properties | Metric | English | Comments | ||
| Rear Barrel Temperature | 235 - 252 °C | 455 - 485 °F | |||
| Middle Barrel Temperature | 246 - 268 °C | 475 - 515 °F | |||
| Front Barrel Temperature | 257 - 274 °C | 495 - 525 °F | |||
| Nozzle Temperature | 252 - 279 °C | 485 - 535 °F | |||
| Melt Temperature | 223 °C | 433 °F | |||
| 252 - 277 °C | 485 - 530 °F | Processing Temperature | |||
| Drying Temperature | 79.4 °C | 175 °F | |||
| Descriptive Properties | |||||
| Suggested Moisture, max | 0.2 | ||||
| Suggested Regrind, max | 25 | ||||