- 脆化温度 [℃]: -21.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.04 g/cc | 1.04 g/cc | ISO 1183 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 95 | 95 | ISO 868, 15 sec | ||
| Tensile Strength | 17.6 MPa | 2550 psi | 500 mm/min, measured parallel to flow; ISO 37 | ||
| Elongation at Break | 390 % | 390 % | 500 mm/min, measured parallel to flow; ISO 37 | ||
| 100% Modulus | 0.0135 GPa | 1.96 ksi | 500 mm/min, measured parallel to flow; ISO 37 | ||
| Tear Strength | 81.0 kN/m | 462 pli | Parallel to flow; ISO 34-B | ||
| 104 kN/m | 593 pli | Perpendicular to flow; ISO 34-B | |||
| Tensile Set | 95 % @Temperature 70.0 °C, Time 79200 sec | 95 % @Temperature 158 °F, Time 22.0 hour | VDA 675 217B | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 165 °C @Time 10800 sec | 329 °F @Time 3.00 hour | no distortion | ||
| Brittleness Temperature | -21.0 °C | -5.80 °F | ASTM D 746 | ||
| Flammability Test | 51 | 51 | mm/min; burn rate | ||
| Descriptive Properties | |||||
| Fogging, Reflectance % | SAE J 1756 | ||||
| Odor Rating | 2 | SAE J1351 / FLTM BO131-01 (dry) | |||
| Ozone Resistance | 0 | 100 pphm / 200 hrs / 20% strain | |||