| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 0.960 g/cc | 0.960 g/cc | ISO 2782 | ||
| Viscosity Measurement | 15 @Temperature 150 °C | 15 @Temperature 302 °F | Kg/cm2; Macklow-Smith extrusion rheometer | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 90 | 90 | ISO 868 | ||
| Tensile Strength | 22.0 MPa | 3190 psi | ISO 37 | ||
| Elongation at Break | 655 % | 655 % | ISO 37 | ||
| 100% Modulus | 0.00530 GPa | 0.769 ksi | ISO 37 | ||
| 200% Modulus | 0.00600 GPa | 0.870 ksi | ISO 37 | ||
| 300% Modulus | 0.00730 GPa | 1.06 ksi | ISO 37 | ||
| Tear Strength | 75.0 kN/m | 428 pli | ISO 34-B | ||
| Abrasion | 85 | 85 | mm3; DIN 53516 | ||
| Compression Set | 35 % @Temperature 22.0 °C, Time 259000 sec | 35 % @Temperature 71.6 °F, Time 72.0 hour | ISO 815 | ||
| 50 % @Temperature 70.0 °C, Time 79200 sec | 50 % @Temperature 158 °F, Time 22.0 hour | ISO 815 | |||
| 65 % @Temperature 100 °C, Time 79200 sec | 65 % @Temperature 212 °F, Time 22.0 hour | ISO 815 | |||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 125 °C | 257 °F | |||
| Minimum Service Temperature, Air | -60.0 °C | -76.0 °F | |||
| Descriptive Properties | |||||
| Bonds with | Polypropylene | ||||
| Chemical Resistance | Acetone | Moderate/Good | |||
| Acids up to 80% | Excellent | ||||
| Alcohol | Excellent | ||||
| Alkalis | Excellent | ||||
| Brake fluid | Good | ||||
| Chlorinate solvents | Poor | ||||
| Diesel | Poor | ||||
| Ethylene glycol | Excellent | ||||
| Gasoline | Good | ||||
| Salt solution | Excellent | ||||
| Soda lye | Excellent | ||||
| Water, 23°C | Excellent | ||||
| Water, 95°C | Good | ||||