| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.12 g/cc | 1.12 g/cc | ISO 2781 | ||
| Viscosity Measurement | 17 @Temperature 180 °C | 17 @Temperature 356 °F | Kg/cm2; Macklow-Smith extrusion rheometer | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 29 | 29 | ISO 868 | ||
| Tensile Strength | 3.50 MPa | 508 psi | ISO 37 | ||
| Elongation at Break | 450 % | 450 % | ISO 37 | ||
| 100% Modulus | 0.000700 GPa | 0.102 ksi | ISO 37 | ||
| Tear Strength | 13.0 kN/m | 74.2 pli | ISO 34-B | ||
| Compression Set | 10 % @Temperature 22.0 °C, Time 259000 sec | 10 % @Temperature 71.6 °F, Time 72.0 hour | ISO 815 | ||
| 17 % @Temperature 70.0 °C, Time 79200 sec | 17 % @Temperature 158 °F, Time 22.0 hour | ISO 815 | |||
| 37 % @Temperature 100 °C, Time 79200 sec | 37 % @Temperature 212 °F, Time 22.0 hour | ISO 815 | |||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 140 °C | 284 °F | |||
| Minimum Service Temperature, Air | -60.0 °C | -76.0 °F | |||
| Descriptive Properties | |||||
| Bonds with | Polypropylene | ||||
| Polypropylene | |||||
| Polypropylene | |||||
| Chemical Resistance | Acetone | Good | |||
| Acids up to 80% | Excellent | ||||
| Alcohol | Excellent | ||||
| Alkalis | Excellent | ||||
| Brake fluid | Good | ||||
| Chlorinate solvents | Poor | ||||
| Diesel | Poor | ||||
| Ethylene glycol | Excellent | ||||
| Gasoline | Poor | ||||
| Salt solution | Excellent | ||||
| Soda lye | Excellent | ||||
| Water, 23°C | Excellent | ||||
| Water, 95°C | Excellent | ||||
| Transparency | Opaque | ||||