- 密度 [g/cm3]: 1.1
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | DIN EN ISO 1183-1:2004 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 90 | 90 | DIN 53505 / ISO 868 | ||
| Tensile Strength at Break | 9.00 MPa | 1310 psi | Deviating from ISO 37 standard test piece is tested with a traverse speed of 200 mm/min; DIN 53504 / ISO 37 | ||
| Elongation at Break | 480 % | 480 % | Deviating from ISO 37 standard test piece is tested with a traverse speed of 200 mm/min; DIN 53504 / ISO 37 | ||
| Graves Tear Strength | 35.0 kN/m | 200 pli | DIN ISO 34-1 Method B (b) | ||
| Compression Set | 25 % @Temperature 23.0 °C, Time 259000 sec | 25 % @Temperature 73.4 °F, Time 72.0 hour | ISO 815 | ||
| 45 % @Temperature 70.0 °C, Time 79200 sec | 45 % @Temperature 158 °F, Time 22.0 hour | ISO 815 | |||
| 68 % @Temperature 100 °C, Time 79200 sec | 68 % @Temperature 212 °F, Time 22.0 hour | ISO 815 | |||
| 78 % @Temperature 120 °C, Time 79200 sec | 78 % @Temperature 248 °F, Time 22.0 hour | ISO 815 | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 180 - 250 °C | 356 - 482 °F | |||
| Descriptive Properties | |||||
| Color | Natural | ||||