- 密度 [g/cm3]: 1.18
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0070 cm/cm | 0.0070 in/in | ASTM D995 |
| Melt Index of Compound | 6.0 g/10 min @Load 21.6 kg, Temperature 210 °C | 6.0 g/10 min @Load 47.6 lb, Temperature 410 °F | cm3/10 min |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 91 | 91 | ASTM D2240 |
| Hardness, Shore D | 41 | 41 | ASTM D2240 |
| Tensile Strength at Break | 55.0 MPa | 7980 psi | DIN 53504 |
| Elongation at Break | 580 % | 580 % | ASTM D412 |
| 100% Modulus | 0.00790 GPa | 1.15 ksi | DIN 53504 |
| 300% Modulus | 0.0123 GPa | 1.78 ksi | DIN 53504 |
| Rebound | 40 % | 40 % | Bayshore; ASTM D2632 |
| Tear Strength | 116 kN/m | 660 pli | ASTM D624 |
| Abrasion | 25 | 25 | [mm3]; ISO 4649 |
| Compression Set | 12 % @Temperature 23.0 °C, Time 252000 sec | 12 % @Temperature 73.4 °F, Time 70.0 hour | ASTM D395 |
| 25 % @Temperature 70.0 °C, Time 86400 sec | 25 % @Temperature 158 °F, Time 24.0 hour | ASTM D395 | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 190 - 200 °C | 374 - 392 °F | Huntsman/TMA |
| Processing Properties | Metric | English | Comments |
| Nozzle Temperature | 205 °C | 401 °F | Injection |
| Zone 1 | 205 °C | 401 °F | Injection |
| Zone 2 | 210 °C | 410 °F | Injection |
| Zone 3 | 210 °C | 410 °F | Injection |
| Mold Temperature | 25.0 - 70.0 °C | 77.0 - 158 °F | Injection |