- 密度 [g/cm3]: 1.19
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0080 cm/cm | 0.0080 in/in | |
| Melt Index of Compound | 5.0 - 10 g/10 min @Load 21.6 kg, Temperature 210 °C | 5.0 - 10 g/10 min @Load 47.6 lb, Temperature 410 °F | cm3/10 min |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 95 | 95 | ASTM D2240 |
| Hardness, Shore D | 47 | 47 | ASTM D2240 |
| Tensile Strength at Break | 53.0 MPa | 7690 psi | ASTM D412 |
| Elongation at Break | 450 % | 450 % | ASTM D412 |
| Tensile Modulus | 0.00700 GPa @Strain 20.0 % | 1.02 ksi @Strain 20.0 % | DIN 53504 |
| 50% Modulus | 0.00900 GPa | 1.31 ksi | DIN 53504 |
| 100% Modulus | 0.0115 GPa | 1.67 ksi | DIN 53504 |
| 200% Modulus | 0.0142 GPa | 2.06 ksi | DIN 53504 |
| 300% Modulus | 0.0204 GPa | 2.96 ksi | DIN 53504 |
| Tear Strength | 105 kN/m | 599 pli | ASTM D624 |
| Abrasion | 35 | 35 | [mm3]; ASTM D395 |
| Compression Set | 14 % @Temperature 23.0 °C, Time 86400 sec | 14 % @Temperature 73.4 °F, Time 24.0 hour | ASTM D395 |
| 23 % @Temperature 70.0 °C, Time 86400 sec | 23 % @Temperature 158 °F, Time 24.0 hour | ASTM D395 | |
| 25 % @Temperature 100 °C, Time 86400 sec | 25 % @Temperature 212 °F, Time 24.0 hour | ASTM D395 | |
| 38 % @Temperature 100 °C, Time 252000 sec | 38 % @Temperature 212 °F, Time 70.0 hour | ASTM D395 | |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 165 °C | 329 °F | DIN 53372 |
| Processing Properties | Metric | English | Comments |
| Nozzle Temperature | 200 °C | 392 °F | Injection |
| Zone 1 | 205 °C | 401 °F | Injection |
| Zone 2 | 205 °C | 401 °F | Injection |
| Zone 3 | 205 °C | 401 °F | Injection |
| Mold Temperature | 25.0 - 70.0 °C | 77.0 - 158 °F | Injection |