- 脆化温度 [℃]: -47.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.04 g/cc | 1.04 g/cc | 23°C; ASTM D792 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 49 | 49 | Air at 212°F, 168 hr; ASTM D573 | ||
| 61 | 61 | Air at 257°F, 168 hr; ASTM D573 | |||
| 53 @Thickness 2.00 mm | 53 @Thickness 0.0787 in | 15 sec; ISO 868 | |||
| Tensile Strength at Break | 1.600 MPa | 232.1 psi | Air at 257°F, 168 hr; ASTM D573 | ||
| 2.954 MPa | 428.4 psi | Air at 212°F, 168 hr; ASTM D573 | |||
| 4.10 MPa | 595 psi | Across Flow; ASTM D412 | |||
| Tensile Stress | 1.00 MPa @Strain 100 % | 145 psi @Strain 100 % | Across Flow; ASTM D412 | ||
| Elongation at Break | 180 % | 180 % | Air at 257°F, 168 hr; ASTM D573 | ||
| 516 % | 516 % | Air at 212°F, 168 hr; ASTM D573 | |||
| 600 % | 600 % | Across Flow; ASTM D412 | |||
| Compression Set | 55 % | 55 % | 257°F, 70 hr; ASTM D395 | ||
| Thermal Properties | Metric | English | Comments | ||
| Brittleness Temperature | -47.0 °C | -52.6 °F | ASTM D746 | ||
| Flammability, UL94 | HB @Thickness 1.10 mm | HB @Thickness 0.0433 in | |||
| HB @Thickness 2.90 mm | HB @Thickness 0.114 in | ||||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 98.9 - 110 °C | 210 - 230 °F | For two-shot injection molding | ||
| 110 - 121 °C | 230 - 250 °F | For insertion injection molding | |||
| Mold Temperature | 25.0 - 50.0 °C | 77.0 - 122 °F | |||
| Descriptive Properties | |||||
| Color | Natural Color | ||||
| Form | Pellets | ||||