| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.24 g/cc | 1.24 g/cc | 23°C; ASTM D792 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 86 | 86 | 2 mm, 15 sec; ISO 868 | ||
| Tensile Strength at Break | 9.03 MPa | 1310 psi | Across Flow; ASTM D412 | ||
| Tensile Stress | 3.90 MPa @Strain 100 % | 566 psi @Strain 100 % | Across Flow; ASTM D412 | ||
| Elongation at Break | 550 % | 550 % | Across Flow; ASTM D412 | ||
| Compression Set | 31 % | 31 % | 73°F, 168 hr; ASTM D395 | ||
| 55 % | 55 % | 212°F, 168 hr; ASTM D395 | |||
| 40 % @Temperature 70.0 °C, Time 79200 sec | 40 % @Temperature 158 °F, Time 22.0 hour | ASTM D395 | |||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Strength | 700 kV/mm @Thickness 2.03 mm | 17800 kV/in @Thickness 0.0799 in | ASTM D149 | ||
| Thermal Properties | Metric | English | Comments | ||
| UL RTI, Electrical | 90.0 °C | 194 °F | UL 746 | ||
| UL RTI, Mechanical with Impact | 85.0 °C @Thickness 1.50 mm | 185 °F @Thickness 0.0591 in | UL 746 | ||
| 90.0 °C @Thickness 3.00 mm | 194 °F @Thickness 0.118 in | UL 746 | |||
| Flammability, UL94 | V-0 @Thickness 3.00 mm | V-0 @Thickness 0.118 in | |||
| V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | ||||
| Oxygen Index | 27 % | 27 % | ASTM D2863 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 175 - 230 °C | 347 - 446 °F | |||
| Mold Temperature | 10.0 - 51.7 °C | 50.0 - 125 °F | Processing | ||
| Drying Temperature | 82.2 °C | 180 °F | |||
| Dry Time | 3 hour | 3 hour | |||
| Moisture Content | 0.080 % | 0.080 % | |||
| Back Pressure | 0.345 - 0.689 MPa | 50.0 - 100 psi | Processing | ||
| Clamp Pressure | 41.4 - 68.9 MPa | 6000 - 10000 psi | |||
| Vent Depth | 0.00254 cm | 0.00100 in | |||
| Cushion | 0.317 - 0.635 cm | 0.125 - 0.250 in | |||
| Screw Speed | 100 - 200 rpm | 100 - 200 rpm | |||
| Descriptive Properties | |||||
| Change in Mass in IRM 903 Oil at 257°F for 70 hr | 41 | ||||
| Color | Natural Color | ||||
| Form | Pellets | ||||
| Injection Rate | Fast | ||||
| Maximum Regrind % | 20 | ||||
| Screw Compression Ratio | 2:1 - 2.5:1 | ||||
| Screw L/D Ratio | 16:1 - 20:1 | ||||