| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.04 g/cc | 1.04 g/cc | ASTM D792 and ISO 1183 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 62 @Time 15.0 sec | 62 @Time 0.00417 hour | 2 mm; ISO 868 | ||
| Tensile Strength at Break | 5.90 MPa | 856 psi | Across Flow; ASTM D412 and ISO 37 | ||
| Tensile Stress | 2.10 MPa @Strain 100 % | 305 psi @Strain 100 % | Across Flow; ASTM D412 and ISO 37 | ||
| Elongation at Break | 470 % | 470 % | Across Flow; ASTM D412 and ISO 37 | ||
| Tear Strength | 28.0 kN/m | 160 pli | Across Flow, Die C; ASTM D624 | ||
| 28.0 kN/m | 160 pli | Across Flow, Method Bb, Angle (Nicked); ISO 34-1 | |||
| Compression Set | 34 % @Temperature 23.0 °C, Time 79200 sec | 34 % @Temperature 73.4 °F, Time 22.0 hour | ASTM D395B Type 1 and ISO 188 Type A | ||
| 62 % @Temperature 70.0 °C, Time 79200 sec | 62 % @Temperature 158 °F, Time 22.0 hour | ASTM D395B Type 1 and ISO 188 Type A | |||
| Descriptive Properties | |||||
| Change in Mass in Air | -1.1% | ASTM D573, 100°C, 168 hr | |||
| Change in Shore Hardness in Air | -2% | Shore A, ASTM D573, 100°C, 672 hr | |||
| Change in Tensile Strength in Air | 0% | ASTM D573, 100°C, 168 hr | |||
| Change in Ultimate Elongation in Air | -11% | ASTM D573, 100°C, 168 hr | |||
| Change in Volume in Air | -1.2% | ASTM D573, 100°C, 168 hr | |||