- 缺口冲击强度: 1.07
- 拉伸强度 [MPa]: 155.0
- 断裂伸长率 [%]: 241
- 弯曲模量 [MPa]: 11.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.63 g/cc | 1.63 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm | 0.0030 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 155 MPa | 22500 psi | ASTM D638 |
| Flexural Yield Strength | 241 MPa | 35000 psi | ASTM D790 |
| Flexural Modulus | 11.0 GPa | 1600 ksi | ASTM D790 |
| Izod Impact, Notched | 1.07 J/cm @Temperature 22.8 °C | 2.00 ft-lb/in @Temperature 73.0 °F | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 290 °C | 554 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 349 - 399 °C | 660 - 750 °F | |
| Mold Temperature | 163 - 218 °C | 325 - 425 °F | |
| Dry Time | <= 3 hour @Temperature 149 °C | <= 3 hour @Temperature 300 °F | to ensure moisture level is below 0.1% |
| Injection Pressure | 49.6 - 74.5 MPa | 7200 - 10800 psi | Secondary |
| 82.7 - 124 MPa | 12000 - 18000 psi | Initial | |
| Back Pressure | 0.000 - 0.345 MPa | 0.000 - 50.0 psi | |
| Shot Size | 30 - 80 % | 30 - 80 % | |
| Screw Speed | 20 - 50 rpm | 20 - 50 rpm | |