- 吸水率 [%]: 0.06
- 拉伸强度 [MPa]: 141.0
- 热变形温度 [℃]: 293.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.48 g/cc | 1.48 g/cc | ISO 1183 | ||
| Water Absorption | 0.060 % | 0.060 % | ISO 62 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 87 | 87 | DIN 53505 | ||
| Tensile Strength at Break | 118 MPa | 17100 psi | ISO 527 | ||
| Tensile Strength, Yield | 141 MPa | 20500 psi | ISO 527 | ||
| Elongation at Break | 3.0 % | 3.0 % | ISO 527 | ||
| Modulus of Elasticity | 8.10 GPa | 1170 ksi | ISO 527 | ||
| Flexural Strength | 210 MPa | 30500 psi | 3.5%; ISO 178 | ||
| Charpy Impact Unnotched | 2.75 J/cm² | 13.1 ft-lb/in² | ISO 179 | ||
| Charpy Impact, Notched | 0.630 J/cm² | 3.00 ft-lb/in² | ISO 179 | ||
| Coefficient of Friction | 0.11 | 0.11 | DIN 53375 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 100000 ohm-cm | >= 100000 ohm-cm | VDE 0303 | ||
| Surface Resistivity per Square | >= 1.00e+7 ohm | >= 1.00e+7 ohm | VDE 0303 | ||
| Dielectric Strength | 24.5 kV/mm | 622 kV/in | VDE 0303 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 22.0 µm/m-°C @Temperature 20.0 °C | 12.2 µin/in-°F @Temperature 68.0 °F | DIN 53752 | ||
| Thermal Conductivity | 0.240 W/m-K | 1.67 BTU-in/hr-ft²-°F | DIN 52612 | ||
| Maximum Service Temperature, Air | 260 °C | 500 °F | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 293 °C | 559 °F | ISO 75 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 277 °C | 531 °F | ISO 75 | ||
| Minimum Service Temperature, Air | -40.0 °C | -40.0 °F | |||
| Flammability, UL94 | V-0 | V-0 | |||
| Descriptive Properties | |||||
| Acid Resistance | limited | ||||
| Aromatic Resistance | yes | ||||
| Bondability | limited | ||||
| CKW Resistance | limited | ||||
| Color | Black | ||||
| Hydrocarbonate Resistance | yes | ||||
| Hydroxide Resistance | yes | ||||
| Ketone Resistance | yes | ||||
| Physiological indifference according | no | ||||
| Resistance Against Hot Water | yes | ||||
| UV Stabilization | yes | ||||