- 弯曲模量 [MPa]: 9.65
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.46 g/cc | 1.46 g/cc | ASTM D792 | ||
| Deformation | 0.10 % | 0.10 % | ASTM D621 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 98 | 98 | ASTM D785 | ||
| Hardness, Shore D | 87 | 87 | ASTM D2240 | ||
| Tensile Strength at Break | 146 MPa | 21200 psi | ASTM D368 | ||
| Elongation at Break | 2.2 % | 2.2 % | ASTM D638 | ||
| Flexural Strength | 188.0 MPa | 27260 psi | |||
| 228 MPa | 33000 psi | ASTM D790 | |||
| 126.8 MPa @Temperature 149 °C | 18390 psi @Temperature 300 °F | ||||
| Flexural Modulus | 9.65 GPa | 1400 ksi | Flexural 0.5% Secant Modulus; ASTM D790 | ||
| 6.55 GPa @Temperature 149 °C | 950 ksi @Temperature 300 °F | ||||
| Compressive Yield Strength | >= 4.14 MPa | >= 600 psi | |||
| Compressive Strength | 170 MPa | 24600 psi | ASTM D695 | ||
| Shear Strength | 68.9 MPa | 10000 psi | Transverse; ASTM D732 | ||
| 89.6 MPa | 13000 psi | Axial; ASTM D732 | |||
| 23.4 MPa @Temperature 260 °C | 3400 psi @Temperature 500 °F | ||||
| 50.3 MPa @Temperature 149 °C | 7300 psi @Temperature 300 °F | ||||
| 68.3 MPa @Temperature 65.6 °C | 9900 psi @Temperature 150 °F | ||||
| Secant Modulus | 11.38 GPa | 1651 ksi | Tensile 0.5% Secant Modulus; ASTM D638 | ||
| Coefficient of Friction, Dynamic | 0.17 | 0.17 | PV=12600 psi-ft./min.; ASTM G77 | ||
| K (wear) Factor | 131 x 10-8 mm³/N-M | 65.0 x 10-10 in³-min/ft-lb-hr | ASTM G77 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 14.4 µm/m-°C @Temperature <=149 °C | 8.00 µin/in-°F @Temperature <=300 °F | ASTM E228 | ||
| 30.6 µm/m-°C @Temperature >=149 °C | 17.0 µin/in-°F @Temperature >=300 °F | ASTM E228 | |||
| Descriptive Properties | |||||
| Color | Black | ||||