Lehmann & Voss LUVOCOM® 1105-0699 PEEK, with carbon fiber, PTFE, lubricant modified

Lehmann & Voss LUVOCOM® 1105-0699 PEEK, with carbon fiber, PTFE, lubricant modified 物性表: Lehmann & Voss LUVOCOM® 1105-0699 PEEK, with carbon fiber, PTFE, lubricant modified物性表及特性介绍,Lehmann & Voss LUVOCOM® 1105-0699 PEEK, with carbon fiber, PTFE, lubricant modified注塑参数详情,如需Lehmann & Voss LUVOCOM® 1105-0699 PEEK, with carbon fiber, PTFE, lubricant modified下载, 可到相关下载区下载
  • 弯曲模量 [MPa]: 19.0
 
Physical PropertiesMetricEnglishComments
Specific Gravity 1.50 g/cc1.50 g/ccISO 1183
Water Absorption <= 0.10 %<= 0.10 %23°C/24h
Linear Mold Shrinkage 0.0010 - 0.0040 cm/cm0.0010 - 0.0040 in/in
 
Mechanical PropertiesMetricEnglishComments
Tensile Stress 210 MPa30500 psi
Elongation at Yield 1.5 %1.5 %
 2.0 %2.0 %flexural
Modulus of Elasticity 24.0 GPa3480 ksi
Flexural Strength 300 MPa43500 psi
Flexural Modulus 19.0 GPa2760 ksi
Charpy Impact Unnotched 4.50 J/cm²21.4 ft-lb/in²edgewise; ISO 179 1eU
 2.80 J/cm²
@Temperature -30.0 °C
13.3 ft-lb/in²
@Temperature -22.0 °F
ISO 179
Charpy Impact, Notched 1.00 J/cm²4.76 ft-lb/in²ISO 179 1eA
 1.00 J/cm²
@Temperature -30.0 °C
4.76 ft-lb/in²
@Temperature -22.0 °F
ISO 179 eA
Coefficient of Friction, Dynamic 0.150.15
Coefficient of Friction, Static 0.120.12
 
Electrical PropertiesMetricEnglishComments
Surface Resistance <= 10000 ohm<= 10000 ohm
Insulation Resistance <= 100000 ohm<= 100000 ohm
 
Thermal PropertiesMetricEnglishComments
CTE, linear 9.00 µm/m-°C5.00 µin/in-°FDIN 53752
Thermal Conductivity 0.550 W/m-K3.82 BTU-in/hr-ft²-°FDIN 52612
Maximum Service Temperature, Air 250 °C482 °F
 280 °C536 °Fshort term
Deflection Temperature at 1.8 MPa (264 psi) 255 °C491 °F
Vicat Softening Point 310 °C590 °FDIN ISO 306
Flammability, UL94 V-0V-0not recognized by UL
 
Processing PropertiesMetricEnglishComments
Processing Temperature 390 °C734 °Fmass temp
Nozzle Temperature 360 - 380 °C680 - 716 °F
Zone 1 360 - 370 °C680 - 698 °F
Zone 2 380 - 390 °C716 - 734 °F
Zone 3 390 - 400 °C734 - 752 °F
Mold Temperature 170 - 200 °C338 - 392 °F
Drying Temperature  120 °C
@Time 21600 - 28800 sec
248 °F
@Time 6.00 - 8.00 hour
or
 150 °C
@Time 10800 - 21600 sec
302 °F
@Time 3.00 - 6.00 hour
Dehumidifying dryer
 
Descriptive Properties
Colornatural color (black)

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-49995.html

免责声明: 本文 Lehmann & Voss LUVOCOM® 1105-0699 PEEK, with carbon fiber, PTFE, lubricant modified 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4