- 缺口冲击强度: 0.881
- 弯曲模量 [MPa]: 18.6
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.42 g/cc | 1.42 g/cc | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 200 MPa | 29000 psi | 50 mm/min; ASTM D638 |
| Elongation at Break | 2.0 % | 2.0 % | 50 mm/min; ASTM D638 |
| Tensile Modulus | 19.54 GPa | 2834 ksi | 50 mm/min; ASTM D638 |
| Flexural Strength | 320 MPa | 46400 psi | 1.3 mm/min; ASTM D790 |
| Flexural Modulus | 18.6 GPa | 2700 ksi | 1.3 mm/min; ASTM D790 |
| Izod Impact, Notched | 0.881 J/cm | 1.65 ft-lb/in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Surface Resistivity per Square | 1000 ohm | 1000 ohm | ASTM D257 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 332 °C @Thickness 3.20 mm | 630 °F @Thickness 0.126 in | Unannealed; ASTM D648 |