- 密度 [g/cm3]: 1.44
- 缺口冲击强度: 0.42
- 弯曲模量 [MPa]: 7.72
- 热变形温度 [℃]: 335.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.45 g/cc | 1.45 g/cc | ASTM D792 |
| Density | 1.44 g/cc | 0.0520 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.0900 % | 0.0900 % | 50% RH, 24 hrs; ASTM D570 |
| 0.100 % | 0.100 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0071 cm/cm @Time 86400 sec | 0.0071 in/in @Time 24.0 hour | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.012 cm/cm @Time 86400 sec | 0.012 in/in @Time 24.0 hour | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 124 MPa | 18000 psi | 5 mm/min; ISO 527 |
| 147 MPa | 21300 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 1.7 % | 1.7 % | 5 mm/min; ISO 527 |
| 2.3 % | 2.3 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 8.62 GPa | 1250 ksi | 1 mm/min; ISO 527 |
| 8.73 GPa | 1270 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 222 MPa | 32200 psi | ISO 178 |
| 228 MPa | 33100 psi | brk, 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 7.72 GPa | 1120 ksi | 2 mm/min; ISO 178 |
| 8.09 GPa | 1170 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.420 J/cm | 0.787 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.84 J/cm | 9.07 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 30.0 kJ/m² | 14.3 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 6.00 J @Temperature 23.0 °C | 4.43 ft-lb @Temperature 73.4 °F | ASTM D3763 |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 28.0 µm/m-°C @Temperature -30.0 - 30.0 °C | 15.6 µin/in-°F @Temperature -22.0 - 86.0 °F | ASTM D696 |
| CTE, linear, Transverse to Flow | 45.0 µm/m-°C @Temperature -30.0 - 30.0 °C | 25.0 µin/in-°F @Temperature -22.0 - 86.0 °F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 335 °C | 635 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 337 °C @Thickness 3.20 mm | 639 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 305 °C | 581 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 320 °C @Thickness 3.20 mm | 608 °F @Thickness 0.126 in | unannealed; ASTM D648 | |