- 密度 [g/cm3]: 1.63
- 缺口冲击强度: 1.05
- 拉伸强度 [MPa]: 116.0
- 断裂伸长率 [%]: 193
- 弯曲模量 [MPa]: 9.97
- 热变形温度 [℃]: 331.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.63 g/cc | 0.0589 lb/in³ | ISO 1183 |
| 1.63 g/cc | 0.0589 lb/in³ | ASTM D 792 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 116 MPa | 16800 psi | 5 mm/min; ISO 527 |
| 144 MPa | 20900 psi | Type I, 5 mm/min; ASTM D 638 | |
| Tensile Strength, Yield | 116 MPa | 16800 psi | 5 mm/min; ISO 527 |
| 144 MPa | 20900 psi | Type I, 5 mm/min; ASTM D 638 | |
| Elongation at Break | 2.0 % | 2.0 % | 5 mm/min; ISO 527 |
| 2.0 % | 2.0 % | Type I, 5 mm/min; ASTM D 638 | |
| Elongation at Yield | 2.0 % | 2.0 % | 5 mm/min; ISO 527 |
| 2.0 % | 2.0 % | Type I, 5 mm/min; ASTM D 638 | |
| Tensile Modulus | 11.43 GPa | 1658 ksi | 1 mm/min; ISO 527 |
| 12.96 GPa | 1880 ksi | 50 mm/min; ASTM D 638 | |
| Flexural Strength | 187 MPa | 27100 psi | ISO 178 |
| 191 MPa | 27700 psi | brk, 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Flexural Yield Strength | 193 MPa | 28000 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Flexural Modulus | 9.97 GPa | 1450 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| 10.35 GPa | 1501 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 1.05 J/cm @Temperature 23.0 °C | 1.97 ft-lb/in @Temperature 73.4 °F | ASTM D 256 |
| Izod Impact, Unnotched | 6.66 J/cm @Temperature 23.0 °C | 12.5 ft-lb/in @Temperature 73.4 °F | ASTM D 4812 |
| Impact Test | 15.0 J @Temperature 23.0 °C | 11.1 ft-lb @Temperature 73.4 °F | Instrumented Impact Total Energy; ASTM D 3763 |
| Coefficient of Friction, Dynamic | 0.46 | 0.46 | ASTM D 3702 Modified |
| Coefficient of Friction, Static | 0.59 | 0.59 | ASTM D 3702 Modified |
| K (wear) Factor | 12.1 x 10-8 mm³/N-M | 6.00 x 10-10 in³-min/ft-lb-hr | Ring; ASTM D 3702 Modified |
| 88.6 x 10-8 mm³/N-M | 44.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D 3702 Modified | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 37.8 µm/m-°C @Temperature -30.0 - 30.0 °C | 21.0 µin/in-°F @Temperature -22.0 - 86.0 °F | ASTM D 696 |
| CTE, linear, Transverse to Flow | 31.8 µm/m-°C @Temperature -30.0 - 30.0 °C | 17.7 µin/in-°F @Temperature -22.0 - 86.0 °F | ASTM D 696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 331 °C | 628 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 329 °C @Thickness 3.20 mm | 624 °F @Thickness 0.126 in | unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 296 °C | 565 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 300 °C @Thickness 3.20 mm | 572 °F @Thickness 0.126 in | unannealed; ASTM D 648 | |