- 密度 [g/cm3]: 1.43
- 缺口冲击强度: 9.0
- 弯曲模量 [MPa]: 22.7
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.43 g/cc | 0.0517 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0020 cm/cm | 0.0010 - 0.0020 in/in | on tensile bar; SABIC Method |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 217 MPa | 31500 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 1.4 % | 1.4 % | 5 mm/min; ISO 527 |
| Flexural Strength | 308 MPa | 44700 psi | break, 2 mm/min; ISO 178 |
| Flexural Modulus | 22.7 GPa | 3290 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² @Temperature 23.0 °C | 4.28 ft-lb/in² @Temperature 73.4 °F | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 40.0 kJ/m² @Temperature 23.0 °C | 19.0 ft-lb/in² @Temperature 73.4 °F | 80*10*4; ISO 180/1U |
| Electrical Properties | Metric | English | Comments |
| Surface Resistance | 10 - 10000 ohm | 10 - 10000 ohm | ASTM D 257 |