Victrex® PEEK 150GL30 30% Glass Fiber Reinforced

Victrex® PEEK 150GL30 30% Glass Fiber Reinforced 物性表: Victrex® PEEK 150GL30 30% Glass Fiber Reinforced物性表及特性介绍,Victrex® PEEK 150GL30 30% Glass Fiber Reinforced注塑参数详情,如需Victrex® PEEK 150GL30 30% Glass Fiber Reinforced下载, 可到相关下载区下载
  • 熔体流动速率 [g/10min]: 16.0
  • 密度 [g/cm3]: 1.51
  • 吸水率 [%]: 0.11
  • 缺口冲击强度: 0.89
  • 断裂伸长率 [%]: 250
  • 弯曲强度 [MPa]: 178.0
  • 弯曲模量 [MPa]: 9.70
  • 硬度: 124.0
  • 脆化温度 [℃]: -65.0
 
Physical PropertiesMetricEnglishComments
Density 1.51 g/cc0.0546 lb/in³ASTM D792
Water Absorption 0.11 %0.11 %24 hrs; ASTM D570
Linear Mold Shrinkage 0.0020 cm/cm0.0020 in/in
Linear Mold Shrinkage, Transverse 0.011 cm/cm0.011 in/in
Melt Flow 16 g/10 min
@Load 5.00 kg,
Temperature 400 °C
16 g/10 min
@Load 11.0 lb,
Temperature 752 °F
Spiral Flow 13.5 cm
@Thickness 1.00 mm
5.31 in
@Thickness 0.0394 in
recommended processing conditions
 
Mechanical PropertiesMetricEnglishComments
Hardness, Rockwell M 103103
Hardness, Rockwell R 124124
Tensile Strength, Ultimate 178 MPa25800 psi
Elongation at Break 2.7 %2.7 %
Modulus of Elasticity 9.70 GPa1410 ksi
Flexural Yield Strength 250 MPa36300 psi
Flexural Modulus 9.70 GPa1410 ksi
Compressive Yield Strength 215 MPa31200 psi
Poissons Ratio 0.450.45
Shear Modulus 3.34 GPa484 ksiCalculated
Izod Impact, Notched 0.890 J/cm1.67 ft-lb/in
Izod Impact, Unnotched 4.54 J/cm8.51 ft-lb/in
 
Electrical PropertiesMetricEnglishComments
Electrical Resistivity 1.00e+16 ohm-cm1.00e+16 ohm-cm
Dielectric Constant  3.2
@Frequency 1000 Hz
3.2
@Frequency 1000 Hz
 3.7
@Frequency 1e+6 Hz
3.7
@Frequency 1e+6 Hz
Dissipation Factor  0.0010
@Frequency 1000 Hz
0.0010
@Frequency 1000 Hz
 0.0040
@Frequency 1e+6 Hz
0.0040
@Frequency 1e+6 Hz
 
Thermal PropertiesMetricEnglishComments
CTE, linear  22.0 µm/m-°C
@Temperature 100 °C
12.2 µin/in-°F
@Temperature 212 °F
 22.0 µm/m-°C
@Temperature 20.0 °C
12.2 µin/in-°F
@Temperature 68.0 °F
Specific Heat Capacity 1.70 J/g-°C0.406 BTU/lb-°F
Thermal Conductivity 0.430 W/m-K2.98 BTU-in/hr-ft²-°F
Melting Point 344 °C651 °F
Maximum Service Temperature, Air 315 °C599 °F
Deflection Temperature at 1.8 MPa (264 psi) 315 °C599 °F
Brittleness Temperature -65.0 °C-85.0 °F
Glass Transition Temp, Tg 143 °C289 °F
UL RTI, Electrical 240 °C464 °F
UL RTI, Mechanical with Impact 220 °C428 °F
UL RTI, Mechanical without Impact 240 °C464 °F
Flammability, UL94 V-0V-0
 
Processing PropertiesMetricEnglishComments
Processing Temperature 380 °C716 °FMiddle Barrel Temp
Rear Barrel Temperature 360 °C680 °F
Middle Barrel Temperature 380 °C716 °F
Front Barrel Temperature 390 °C734 °F
Nozzle Temperature 390 °C734 °F
Mold Temperature 180 °C356 °F
Drying Temperature 150 °C302 °F
Dry Time 3 hour3 hour

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-50324.html

免责声明: 本文 Victrex® PEEK 150GL30 30% Glass Fiber Reinforced 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4