- 缺口冲击强度: 8.5
- 拉伸强度 [MPa]: 290.0
- 弯曲模量 [MPa]: 19.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.36 g/cc @Temperature 23.0 °C | 1.36 g/cc @Temperature 73.4 °F | ISO 1183 |
| Viscosity | 200000 cP @Temperature 400 °C | 200000 cP @Temperature 752 °F | 0.5mm die; Victrex test method |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 290 MPa @Temperature 23.0 °C | 42100 psi @Temperature 73.4 °F | ISO 527 |
| Elongation at Yield | 1.9 % @Temperature 23.0 °C | 1.9 % @Temperature 73.4 °F | ISO 527 |
| Tensile Modulus | 22.0 GPa @Temperature 23.0 °C | 3190 ksi @Temperature 73.4 °F | ISO 527 |
| Flexural Strength | 400 MPa @Temperature 23.0 °C | 58000 psi @Temperature 73.4 °F | ISO 178 |
| Flexural Modulus | 19.0 GPa @Temperature 23.0 °C | 2760 ksi @Temperature 73.4 °F | ISO 178 |
| Izod Impact, Notched (ISO) | 8.50 kJ/m² @Temperature 23.0 °C | 4.04 ft-lb/in² @Temperature 73.4 °F | ISO 180 |
| Izod Impact, Unnotched (ISO) | 55.0 kJ/m² @Temperature 23.0 °C | 26.2 ft-lb/in² @Temperature 73.4 °F | ISO 180 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 347 °C | 657 °F | ISO 75A-f |
| Processing Properties | Metric | English | Comments |
| Feed Temperature | 70.0 - 100 °C | 158 - 212 °F | |
| Rear Barrel Temperature | >= 400 °C | >= 752 °F | |
| Middle Barrel Temperature | >= 400 °C | >= 752 °F | |
| Front Barrel Temperature | >= 400 °C | >= 752 °F | |
| Mold Temperature | 175 - 205 °C | 347 - 401 °F | |
| Drying Temperature | >= 150 °C @Time 10800 sec | >= 302 °F @Time 3.00 hour | |
| >= 160 °C @Time 7200 sec | >= 320 °F @Time 2.00 hour | ||