Victrex® PEEK 90GL30 Polyetheretherketone, 30% Glass Fiber Reinforced

Victrex® PEEK 90GL30 Polyetheretherketone, 30% Glass Fiber Reinforced 物性表: Victrex® PEEK 90GL30 Polyetheretherketone, 30% Glass Fiber Reinforced物性表及特性介绍,Victrex® PEEK 90GL30 Polyetheretherketone, 30% Glass Fiber Reinforced注塑参数详情,如需Victrex® PEEK 90GL30 Polyetheretherketone, 30% Glass Fiber Reinforced下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.52
  • 吸水率 [%]: 0.04
  • 缺口冲击强度: 8.5
  • 弯曲模量 [MPa]: 12.0
 
Physical PropertiesMetricEnglishComments
Density 1.52 g/cc0.0549 lb/in³Crystalline; ISO 1183
Water Absorption 0.040 %
@Temperature 23.0 °C,
Time 86400 sec
0.040 %
@Temperature 73.4 °F,
Time 24.0 hour
3.2mm thick tensile bar; ISO 62-1
Water Absorption at Saturation 0.30 %
@Temperature 23.0 °C
0.30 %
@Temperature 73.4 °F
Equilibrium; by immersion; ISO 62-1
Viscosity 220000 cP
@Temperature 400 °C
220000 cP
@Temperature 752 °F
melt; ISO 11443
Linear Mold Shrinkage, Flow 0.0030 cm/cm0.0030 in/in360°C nozzle, 160°C tool; ISO 294-4
Linear Mold Shrinkage, Transverse 0.0090 cm/cm0.0090 in/in370°C nozzle, 180°C tool; ISO 294-4
Spiral Flow  18.5 cm
@Thickness 1.00 mm
7.28 in
@Thickness 0.0394 in
370°C nozzle, 180°C tool
 22.0 cm
@Thickness 1.00 mm
8.66 in
@Thickness 0.0394 in
400°C nozzle, 200°C tool
 
Mechanical PropertiesMetricEnglishComments
Hardness, Shore D 90
@Temperature 23.0 °C
90
@Temperature 73.4 °F
ISO 868
Tensile Strength at Break  45.0 MPa
@Temperature 275 °C
6530 psi
@Temperature 527 °F
ISO 527
 60.0 MPa
@Temperature 225 °C
8700 psi
@Temperature 437 °F
ISO 527
 80.0 MPa
@Temperature 175 °C
11600 psi
@Temperature 347 °F
ISO 527
 130 MPa
@Temperature 125 °C
18900 psi
@Temperature 257 °F
ISO 527
 190 MPa
@Temperature 23.0 °C
27600 psi
@Temperature 73.4 °F
ISO 527
Elongation at Break 2.3 %
@Temperature 23.0 °C
2.3 %
@Temperature 73.4 °F
ISO 527
Tensile Modulus 12.0 GPa
@Temperature 23.0 °C
1740 ksi
@Temperature 73.4 °F
ISO 527
Flexural Strength  50.0 MPa
@Temperature 275 °C
7250 psi
@Temperature 527 °F
ISO 178
 80.0 MPa
@Temperature 175 °C
11600 psi
@Temperature 347 °F
ISO 178
 190 MPa
@Temperature 125 °C
27600 psi
@Temperature 257 °F
ISO 178
 290 MPa
@Temperature 23.0 °C
42100 psi
@Temperature 73.4 °F
ISO 178
Flexural Modulus 12.0 GPa
@Temperature 23.0 °C
1740 ksi
@Temperature 73.4 °F
ISO 178
Compressive Strength  55.0 MPa
@Temperature 250 °C
7980 psi
@Temperature 482 °F
ISO 604
 160 MPa
@Temperature 120 °C
23200 psi
@Temperature 248 °F
ISO 604
 250 MPa
@Temperature 23.0 °C
36300 psi
@Temperature 73.4 °F
ISO 604
Izod Impact, Notched (ISO) 8.50 kJ/m²
@Temperature 23.0 °C
4.04 ft-lb/in²
@Temperature 73.4 °F
ISO 180/A
Izod Impact, Unnotched (ISO) 40.0 kJ/m²
@Temperature 23.0 °C
19.0 ft-lb/in²
@Temperature 73.4 °F
ISO 180/U
Charpy Impact Unnotched 4.50 J/cm²
@Temperature 23.0 °C
21.4 ft-lb/in²
@Temperature 73.4 °F
ISO 179/1U
Charpy Impact, Notched 0.750 J/cm²
@Temperature 23.0 °C
3.57 ft-lb/in²
@Temperature 73.4 °F
ISO 179/1eA
 
Electrical PropertiesMetricEnglishComments
Volume Resistivity 1.00e+16 ohm-cm1.00e+16 ohm-cmIEC 60093
Dielectric Constant 3.3
@Frequency 1000 Hz,
Temperature 23.0 °C
3.3
@Frequency 1000 Hz,
Temperature 73.4 °F
IEC 60250
Dielectric Strength 17.0 kV/mm
@Thickness 2.50 mm
432 kV/in
@Thickness 0.0984 in
IEC 60243-1
Dissipation Factor 0.0040
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C
0.0040
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F
IEC 60250
 
Thermal PropertiesMetricEnglishComments
CTE, linear  20.0 µm/m-°C
@Temperature >=143 °C
11.1 µin/in-°F
@Temperature >=289 °F
Along flow above Tg; ISO 11359
 20.0 µm/m-°C
@Temperature <=143 °C
11.1 µin/in-°F
@Temperature <=289 °F
Along flow below Tg; ISO 11359
 45.0 µm/m-°C
@Temperature <=143 °C
25.0 µin/in-°F
@Temperature <=289 °F
Average below Tg; ISO 11359
 110 µm/m-°C
@Temperature >=143 °C
61.1 µin/in-°F
@Temperature >=289 °F
Average above Tg; ISO 11359
Specific Heat Capacity 1.70 J/g-°C
@Temperature 23.0 °C
0.406 BTU/lb-°F
@Temperature 73.4 °F
DSC
Thermal Conductivity 0.300 W/m-K
@Temperature 23.0 °C
2.08 BTU-in/hr-ft²-°F
@Temperature 73.4 °F
ISO/CD 22007-4
Melting Point 343 °C649 °FISO 11357
Deflection Temperature at 1.8 MPa (264 psi) 335 °C635 °FISO 75A-f
Glass Transition Temp, Tg 143 °C289 °FOnset; ISO 11357
Flammability, UL94 V-0
@Thickness 0.500 mm
V-0
@Thickness 0.0197 in
Glow Wire Test 960 °C
@Thickness 2.00 mm
1760 °F
@Thickness 0.0787 in
IEC 60695-2-12
 
Processing PropertiesMetricEnglishComments
Mold Temperature 170 - 200 °C338 - 392 °F
Drying Temperature  120 °C
@Time 18000 sec
248 °F
@Time 5.00 hour
 150 °C
@Time 10800 sec
302 °F
@Time 3.00 hour

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-50368.html

免责声明: 本文 Victrex® PEEK 90GL30 Polyetheretherketone, 30% Glass Fiber Reinforced 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络