- 密度 [g/cm3]: 1.3
- 缺口冲击强度: 7.5
- 拉伸强度 [MPa]: 90.0
- 弯曲模量 [MPa]: 4.10
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 0.250 g/cc | 0.00903 lb/in³ | ISO 1183 | ||
| Density | 1.30 g/cc | 0.0470 lb/in³ | ISO 1183 | ||
| Particle Size | 70 µm | 70 µm | D50; ISO 13320-1 | ||
| Viscosity | 450000 cP @Temperature 400 °C | 450000 cP @Temperature 752 °F | Melt; ISO 11443 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 90.0 MPa | 13100 psi | Result based on similar products; ISO 527 | ||
| Elongation at Break | 30 % | 30 % | Result based on similar products; ISO 527 | ||
| Tensile Modulus | 3.70 GPa | 537 ksi | Result based on similar products; ISO 527 | ||
| Flexural Strength | 150 MPa | 21800 psi | Result based on similar products; ISO 178 | ||
| Flexural Modulus | 4.10 GPa | 595 ksi | Result based on similar products; ISO 178 | ||
| Izod Impact, Notched (ISO) | 7.50 kJ/m² | 3.57 ft-lb/in² | Result based on similar products; ISO 180/A | ||
| Izod Impact, Unnotched (ISO) | NB | NB | Result based on similar products; ISO 180/U | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 343 °C | 649 °F | ISO 11357 | ||
| Glass Transition Temp, Tg | 143 °C | 289 °F | Onset; ISO 11357 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 380 - 400 °C | 716 - 752 °F | |||
| Dry Time | 3 hour @Temperature 150 °C | 3 hour @Temperature 302 °F | |||
| 5 hour @Temperature 120 °C | 5 hour @Temperature 248 °F | ||||
| Descriptive Properties | |||||
| Color | Natural | ||||