PA66 80G14AHS NC010 性状为半透明或不透明乳白色结晶形聚合物，具有可塑性。密度1．15g／cm3。熔点252℃。脆化温度-30℃。热分解温度大于350℃。连续耐热80-120℃,平衡吸水率2．5％。能耐酸、碱、大多数无机盐水溶液、卤代烷、烃类、酯类、酮类等腐蚀，但易溶于苯酚、甲酸等极性溶剂。

Physical Properties	Metric	English	Comments
物性表：
Density	1.19 g/cc	0.0430 lb/in³	DAM; ISO 1183
Moisture Absorption	1.90 % @Thickness 2.00 mm	1.90 % @Thickness 0.0787 in	DAM; Sim. to ISO 62
Linear Mold Shrinkage, Flow	0.0070 cm/cm	0.0070 in/in	DAM; ISO 294-4 2577
Linear Mold Shrinkage, Transverse	0.0080 cm/cm	0.0080 in/in	DAM; ISO 294-4 2577

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	72.0 MPa	10400 psi	50%RH; ISO 527-1/-2
	110 MPa	16000 psi	DAM; ISO 527-1/-2
Elongation at Break	3.8 %	3.8 %	DAM; ISO 527-1/-2
	9.0 %	9.0 %	50%RH; ISO 527-1/-2
Tensile Modulus	3.30 GPa	479 ksi	50%RH; ISO 527-1/-2
	5.00 GPa	725 ksi	DAM; ISO 527-1/-2
Flexural Modulus	3.12 GPa	453 ksi	50%RH; ISO 178
	4.40 GPa	638 ksi	DAM; ISO 178
Izod Impact, Notched (ISO)	13.0 kJ/m²	6.19 ft-lb/in²	DAM; ISO 180/1A
	6.00 kJ/m² @Temperature -40.0 °C	2.86 ft-lb/in² @Temperature -40.0 °F	DAM; ISO 180/1A
Charpy Impact Unnotched	7.30 J/cm²	34.7 ft-lb/in²	DAM; ISO 179/1eU
	7.60 J/cm²	36.2 ft-lb/in²	50%RH; ISO 179/1eU
	7.10 J/cm² @Temperature -30.0 °C	33.8 ft-lb/in² @Temperature -22.0 °F	50%RH; ISO 179/1eU
Charpy Impact, Notched	1.30 J/cm²	6.19 ft-lb/in²	DAM; ISO 179/1eA
	1.70 J/cm²	8.09 ft-lb/in²	50%RH; ISO 179/1eA
	0.600 J/cm² @Temperature -40.0 °C	2.86 ft-lb/in² @Temperature -40.0 °F	50%RH; ISO 179/1eA
	0.700 J/cm² @Temperature -30.0 °C	3.33 ft-lb/in² @Temperature -22.0 °F	50%RH; ISO 179/1eA
	0.900 J/cm² @Temperature -30.0 °C	4.28 ft-lb/in² @Temperature -22.0 °F	DAM; ISO 179/1eA

Electrical Properties	Metric	English	Comments
Dissipation Factor	0.018 @Frequency 100 Hz	0.018 @Frequency 100 Hz	50%RH; IEC 60250
	0.027 @Frequency 100 Hz	0.027 @Frequency 100 Hz	DAM; IEC 60250

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	40.0 µm/m-°C	22.2 µin/in-°F	DAM; ISO 11359-1/-2
CTE, linear, Transverse to Flow	120 µm/m-°C	66.7 µin/in-°F	DAM; ISO 11359-1/-2
Melting Point	263 °C	505 °F	DAM; 10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)	221 °C	430 °F	DAM; ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)	240 °C	464 °F	DAM; ISO 75-1/-2
Vicat Softening Point	215 °C	419 °F	DAM; 50°C/h 50N; ISO 306
Flammability, UL94	HB @Thickness 1.50 mm	HB @Thickness 0.0591 in	DAM; IEC 60695-11-10
	HB @Thickness 0.800 mm	HB @Thickness 0.0315 in	DAM; IEC 60695-11-10
Flame Spread	44 mm/min @Thickness 1.00 mm	1.7 in/min @Thickness 0.0394 in	ISO 3795 (FMVSS 302)

Descriptive Properties
Additives	Release agent
Delivery form	Pellets
Part Marking Code	>PA66-IGF14<	ISO 11469
Processing	Injection Moulding
Regional Availability	Asia Pacific
	Europe
	Global
	Near East/Africa
	North America
	South and Central America
Resin Identification	PA66-IGF14
Special characteristics	Heat stabilised or stable to heat

具有优良的耐磨性、自润滑性，机械强度较高。但吸水性较大，因而尺寸稳定性较差。广泛用于制造机械、汽车、化学与电气装置的零件，如齿轮、滚子、滑轮、辊轴、泵体中叶轮、风扇叶片、高压密封围、阀座、垫片、衬套、各种把手、支撑架、电线包层等。亦可制成薄膜用作包装材料。
H颗粒05

图：