PA6 TG3S BK-104 15%玻璃、_产品资讯

PA6 TG3S 性状为半透明或不透明乳白色结晶形聚合物，具有可塑性。密度1．15g／cm3。熔点252℃。脆化温度-30℃。热分解温度大于350℃。连续耐热80-120℃,平衡吸水率2．5％。能耐酸、碱、大多数无机盐水溶液、卤代烷、烃类、酯类、酮类等腐蚀，但易溶于苯酚、甲酸等极性溶剂。具有优良的耐磨性、自润滑性，机械强度较高。但吸水性较大，因而尺寸稳定性较差。

颗粒：

、

物性表:

Physical Properties	Metric	English	Comments

Density	1.20 g/cc	0.0434 lb/in³	ISO 1183
Linear Mold Shrinkage	0.0050 cm/cm	0.0050 in/in	ASTM Data; MD

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	93.0 MPa	13500 psi	0.2 in/min; ASTM Test
Tensile Strength, Ultimate	93.0 MPa	13500 psi	5mm/min; ISO 527
Elongation at Break	3.0 %	3.0 %	5mm/min; ISO 527
Flexural Strength	150 MPa	21800 psi	ASTM Test
Flexural Modulus	4.39 GPa	637 ksi	ISO Data
	4.48 GPa	650 ksi	ASTM Test
Izod Impact, Notched	1.55 J/cm @Thickness 3.17 mm	2.90 ft-lb/in @Thickness 0.125 in	ASTM Test
Izod Impact, Notched (ISO)	17.0 kJ/m²	8.09 ft-lb/in²	ISO Test
	5.40 kJ/m² @Temperature -40.0 °C	2.57 ft-lb/in² @Temperature -40.0 °F	ISO Test
Charpy Impact, Notched	1.38 J/cm²	6.57 ft-lb/in²	ISO 179

Thermal Properties	Metric	English	Comments
Melting Point	220 °C	428 °F	10 K/min
	220 °C	428 °F	ASTM Test
Deflection Temperature at 0.46 MPa (66 psi)	211 °C	412 °F	ISO 75
	211 °C	412 °F	ASTM Test
Deflection Temperature at 1.8 MPa (264 psi)	180 °C	356 °F	ISO 75
	190 °C	374 °F	ASTM Test
Flammability, UL94	HB @Thickness 1.00 mm	HB @Thickness 0.0394 in
	HB @Thickness 3.00 mm	HB @Thickness 0.118 in

Descriptive Properties
Color	BK-104
Commercial Status	Active America
Impact Modified	Yes
Primary Processing Technique	Injection Molding
UL.UL-C	Yes

广泛用于制造机械、汽车、化学与电气装置的零件，如齿轮、滚子、滑轮、辊轴、泵体中叶轮、风扇叶片、高压密封围、阀座、垫片、衬套、各种把手、支撑架、电线包层等。亦可制成薄膜用作包装材料。此外，还可用于制作医疗器械、体育用品、日用品等。

上海松翰塑化科技有限公司，供应原料，品质真实,物实价廉。

PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。