- 密度 [g/cm3]: 1.13
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 1.13 g/cc | 0.0408 lb/in³ | |
| Density | 1.13 g/cc | 0.0408 lb/in³ | |
| Thickness | 610 microns | 24.0 mil | Nominal |
| 612 microns | 24.1 mil | Typical; ASTM D374 | |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 18 % | 18 % | ASTM D828 |
| Film Elongation at Break, TD | 14 % | 14 % | ASTM D828 |
| Tear Strength, Total | 157 N | 35.3 lb (f) | Initial in TD; ASTM D1004 |
| 201 N | 45.2 lb (f) | Initial in MD; ASTM D1004 | |
| Film Tensile Strength at Break, MD | 121.1 MPa | 17560 psi | Calculated from mfr's report of 741 N/cm per ASTM D828 and the typical thickness |
| Film Tensile Strength at Break, TD | 81.2 MPa | 11800 psi | Calculated from mfr's report of 497 N/cm per ASTM D828 and the typical thickness |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 2.00e+16 ohm-cm | 2.00e+16 ohm-cm | 50% RH; tested on 10 mil thickness sample; ASTM D257 |
| Surface Resistivity per Square | 2.00e+16 ohm | 2.00e+16 ohm | tested on 10 mil thickness sample; ASTM D257 |
| Dielectric Constant | 3.7 @Frequency 60 Hz | 3.7 @Frequency 60 Hz | ASTM D150 |
| Dielectric Strength | 31.0 kV/mm | 787 kV/in | AC Rapid Rise; ASTM D149 |
| Dissipation Factor | 0.0070 @Frequency 60 Hz | 0.0070 @Frequency 60 Hz | ASTM D150 |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 220 °C | 428 °F | 220°C insulation by UL, the US Navy, and other tests |
| Oxygen Index | 27 - 32 % | 27 - 32 % | Range at RT for Type 410; depends on thickness and density |
| Shrinkage, MD | 0.00 % | 0.00 % | at 300°C |
| Shrinkage, TD | 0.00 % | 0.00 % | at 300°C |