| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Thickness | 76.2 microns | 3.00 mil | Polyethylene Interleave | ||
| 127 microns | 5.00 mil | Kodacel Substrate | |||
| 2870 - 3480 microns | 113 - 137 mil | Side 1 | |||
| 2870 - 3480 microns | 113 - 137 mil | Overall | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 50 - 60 | 50 - 60 | Compound Property | ||
| Tensile Strength | >= 6.89 MPa | >= 1000 psi | Compound Property | ||
| Elongation at Break | >= 500 % | >= 500 % | Compound Property | ||
| 100% Modulus | >= 1.72 GPa | >= 250 ksi | |||
| Tear Strength | >= 35.1 kN/m | >= 200 pli | Compound Property | ||
| Compression Set | <= 28 % | <= 28 % | After Post Cure, Compound Property | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 232 °C | 450 °F | |||
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 30.0 min @Temperature 177 °C | 0.500 hour @Temperature 350 °F | Recommended Cure Cycle | ||
| 240 min @Temperature 227 °C | 4.00 hour @Temperature 440 °F | Recommended Postcure Cycle | |||
| Shelf Life | 3.00 Month @Temperature 4.44 °C | 3.00 Month @Temperature 40.0 °F | From date of manufacture | ||
| Descriptive Properties | |||||
| Color | Naturally Translucent | ||||
| Total Product Weight (oz/yd2) | 103.5 - 132.5 | ||||