- 密度 [g/cm3]: 1.3
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in³ | Silicone Property; Arlon SQA-TMS-024 | ||
| Thickness | 50.8 microns | 2.00 mil | Side 1; Arlon SQA-TMS-003 | ||
| 63.5 microns | 2.50 mil | Interleave | |||
| 76.2 microns | 3.00 mil | Substrate; Arlon SQA-TMS-003 | |||
| 127 microns | 5.00 mil | Overall; Arlon SQA-TMS-003 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 55 | 55 | Silicone Property; ASTM D2240 | ||
| Tensile Strength | 6.72 MPa | 975 psi | Silicone Property; ASTM D412 | ||
| Elongation at Break | 275 % | 275 % | Silicone Property; ASTM D412 | ||
| Tear Strength | 9.64 kN/m | 55.0 pli | Die B, Silicone Property; ASTM D624 | ||
| Peel Strength | 0.701 kN/m | 4.00 pli | Bond Strength; Arlon SQA-TMS-011 | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Strength | 35.4 kV/mm | 900 kV/in | ASTM D149 | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 232 °C | 450 °F | |||
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |||
| Flammability Test | >= 1.0 | >= 1.0 | [sec], Flame and Glow; FAR 25.853 App.F, P.1,.Aii | ||
| >= 1.0 | >= 1.0 | [in], Char Length; FAR 25.853 App.F, P.1,.Aii | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 120 min @Temperature 204 °C | 2.00 hour @Temperature 400 °F | Recommended Postcure Cycle | ||
| 15.0 min @Pressure 0.345 MPa, Temperature 149 °C | 0.250 hour @Pressure 50.0 psi, Temperature 300 °F | Recommended Cure Cycle | |||
| Shelf Life | 6.00 Month @Temperature 21.1 °C | 6.00 Month @Temperature 70.0 °F | From date of manufacture | ||
| Descriptive Properties | |||||
| Color | Red | ||||
| Red | Substrate | ||||
| Total Product Weight (oz/yd2) | 4.8 | Arlon SQA-TMS-025 | |||