- 密度 [g/cm3]: 1.375
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.375 g/cc | 0.04968 lb/in³ | Silicone Property; Arlon SQA-TMS-024 | ||
| Thickness | 63.5 microns | 2.50 mil | Interleave | ||
| 152 microns | 6.00 mil | Layer 2; Arlon SQA-TMS-003 | |||
| 356 microns | 14.0 mil | Layer 1; Arlon SQA-TMS-003 | |||
| 508 microns | 20.0 mil | Substrate; Arlon SQA-TMS-003 | |||
| 1020 microns | 40.0 mil | Overall; Arlon SQA-TMS-003 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 35 | 35 | Silicone Property; ASTM D2240 | ||
| Tensile Strength | 6.21 MPa | 900 psi | Silicone Property; ASTM D412 | ||
| Elongation at Break | 750 % | 750 % | Silicone Property; ASTM D412 | ||
| Peel Strength | 7.05 kN/m | 40.2 pli | (S1 to S1) Bond Strength; Arlon SQA -TMS-011 | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Strength | 18.2 kV/mm | 462 kV/in | ASTM D149 | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 232 °C | 450 °F | |||
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |||
| Flammability Test | <= 3.0 | <= 3.0 | [in], Char Length; FAR25.853 Appendix F Pt. 1 Section (a),(1).(ii) | ||
| <= 15 | <= 15 | [sec], Flame and Glow Time; FAR25.853 Appendix F Pt. 1 Section (a),(1).(ii) | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 120 min @Temperature 204 °C | 2.00 hour @Temperature 400 °F | Recommended Postcure Cycle | ||
| 15.0 min @Pressure 0.345 MPa, Temperature 121 °C | 0.250 hour @Pressure 50.0 psi, Temperature 250 °F | Recommended Cure Cycle | |||
| Shelf Life | 6.00 Month @Temperature 21.1 °C | 6.00 Month @Temperature 70.0 °F | From date of manufacture | ||
| Descriptive Properties | |||||
| Color | Light Yellow | Substrate | |||
| Red | |||||
| Total Product Weight (oz/yd2) | 35.3 | Arlon SQA-TMS-025 | |||