| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Thickness | 12.7 microns | 0.500 mil | Side 1, Skim Coat | ||
| 50.8 microns | 2.00 mil | Side 2, Cured | |||
| 76.2 microns | 3.00 mil | Polyethylene, Interleave | |||
| >= 203 microns | >= 8.00 mil | Side 2, Uncured | |||
| 457 microns | 18.0 mil | Prime Coated 162 Fiberglass, Substrate | |||
| 749 - 876 microns | 29.5 - 34.5 mil | Overall | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 60 - 70 | 60 - 70 | Compound Property | ||
| Tensile Strength | >= 5.86 MPa | >= 850 psi | Compound Property | ||
| Elongation at Break | >= 200 % | >= 200 % | Compound Property | ||
| Peel Strength | >= 1.05 kN/m | >= 6.00 pli | Bond Strength | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Strength | >= 15.7 kV/mm | >= 400 kV/in | |||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 232 °C | 450 °F | |||
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |||
| Flammability, UL94 | V-0 | V-0 | Compound Rated | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 15.0 min @Temperature 177 °C | 0.250 hour @Temperature 350 °F | Recommended Cure Cycle | ||
| 120 min @Temperature 204 °C | 2.00 hour @Temperature 400 °F | Recommended Postcure Cycle | |||
| Shelf Life | 6.00 Month | 6.00 Month | From date of manufacture | ||
| Descriptive Properties | |||||
| Color | Blue Gray | ||||
| Total Product Weight (oz/yd2) | 29 - 33 | ||||
| Uncoated Fabric Break Strength | 420 lb/in | Fill Direction, Substrate Property | |||
| 700 lb/in | Warp Direction, Substrate Property | ||||