- 拉伸强度 [MPa]: 66.9
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.35 - 1.45 g/cc @Thickness 1.57 mm | 1.35 - 1.45 g/cc @Thickness 0.0620 in | ASTM D792 | ||
| Moisture Absorption at Equilibrium | 2.4 % @Thickness 1.57 mm | 2.4 % @Thickness 0.0620 in | ASTM D229 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 90 - 110 @Thickness 1.57 mm | 90 - 110 @Thickness 0.0620 in | ASTM D785 | ||
| Tensile Strength, Yield | 66.9 MPa @Thickness 1.57 mm | 9700 psi @Thickness 0.0620 in | CW; ASTM D638 | ||
| 96.5 MPa @Thickness 1.57 mm | 14000 psi @Thickness 0.0620 in | LW; ASTM D638 | |||
| Modulus of Elasticity | 7.58 GPa @Thickness 1.57 mm | 1100 ksi @Thickness 0.0620 in | CW; ASTM D229 | ||
| 10.3 GPa @Thickness 1.57 mm | 1500 ksi @Thickness 0.0620 in | LW; ASTM D229 | |||
| Flexural Strength | 124 MPa @Thickness 1.57 mm | 18000 psi @Thickness 0.0620 in | CW; ASTM D790 | ||
| 164 MPa @Thickness 1.57 mm | 23800 psi @Thickness 0.0620 in | LW; ASTM D790 | |||
| Compressive Strength | 269 MPa @Thickness 12.7 mm | 39000 psi @Thickness 0.500 in | ASTM D695 | ||
| Shear Strength | 100 MPa @Thickness 15.7 mm | 14500 psi @Thickness 0.620 in | ASTM D732 | ||
| Izod Impact, Unnotched | 0.694 J/cm @Thickness 12.7 mm | 1.30 ft-lb/in @Thickness 0.500 in | CW, Cond E-48/50; ASTM D256 | ||
| 0.854 J/cm @Thickness 12.7 mm | 1.60 ft-lb/in @Thickness 0.500 in | LW, Cond E-48/50; ASTM D256 | |||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Breakdown | 5000 V @Thickness 1.57 mm | 5000 V @Thickness 0.0620 in | Cond D-48/50; ASTM D229 S/S | ||
| 30000 V @Thickness 1.57 mm | 30000 V @Thickness 0.0620 in | Cond A; ASTM D229 S/S | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 10.0 µm/m-°C @Thickness 1.57 mm, Temperature 20.0 °C | 5.56 µin/in-°F @Thickness 0.0620 in, Temperature 68.0 °F | x-axis; IPC-TM 650-2.4.24 | ||
| CTE, linear, Transverse to Flow | 12.0 µm/m-°C @Thickness 1.57 mm, Temperature 20.0 °C | 6.67 µin/in-°F @Thickness 0.0620 in, Temperature 68.0 °F | x-axis; IPC-TM 650-2.4.24 | ||
| Maximum Service Temperature, Air | 130 °C | 266 °F | |||
| Flammability, UL94 | HB @Thickness 1.57 mm | HB @Thickness 0.0620 in | |||
| Descriptive Properties | |||||
| Bond Strength | 1900 lb | 0.5", ASTM D229 | |||
| Color | Black | ||||