- 弯曲强度 [MPa]: 6.89
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.10 g/cc | 1.10 g/cc | silicone property; Arlon SQA-TMS-024 | ||
| Thickness | 254 microns | 10.0 mil | overall; Arlon SQA-TMS-003 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 18 | 18 | silicone property; ASTM D2240 | ||
| Tensile Strength, Ultimate | 6.89 MPa | 1000 psi | silicone property; ASTM D412 | ||
| Elongation at Break | 950 % | 950 % | silicone property; ASTM D412 | ||
| Modulus of Elasticity | 0.000517 GPa | 0.0750 ksi | silicone property; Arlon SQA-TMS-008 | ||
| Poissons Ratio | 0.50 | 0.50 | silicone property | ||
| Shear Strength | 3.45 MPa | 500 psi | silicone property; ASTM D1002 | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Strength | 39.4 kV/mm | 1000 kV/in | ASTM D149 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 335 µm/m-°C @Temperature 20.0 °C | 186 µin/in-°F @Temperature 68.0 °F | silicone property; ASTM E 831 | ||
| Thermal Conductivity | 0.900 W/m-K | 6.25 BTU-in/hr-ft²-°F | silicone property; Arlon SQA-TMS-022 | ||
| Maximum Service Temperature, Air | 204 °C | 400 °F | |||
| Minimum Service Temperature, Air | -51.1 °C | -60.0 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 15.0 min @Pressure 0.103 - 0.345 MPa, Temperature 121 °C | 0.250 hour @Pressure 15.0 - 50.0 psi, Temperature 250 °F | |||
| Shelf Life | 6.00 Month @Temperature 7.22 °C | 6.00 Month @Temperature 45.0 °F | |||
| Descriptive Properties | |||||
| Appearance | Translucent | ||||