- 密度 [g/cm3]: 1.4
- 弯曲强度 [MPa]: 0.517
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in³ | ASTM D1475 |
| Outgassing - Total Mass Loss | 0.11 % | 0.11 % | Cured property; at 10E-6 torr; ASTM E595 |
| Collected Volatile Condensable Material | 0.02 % | 0.02 % | Cured property; at 10E-6 torr; ASTM E595 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | <= 3 | <= 3 | Cured property; ASTM D2240 |
| Tensile Strength, Ultimate | 0.517 MPa @Thickness 1.57 mm | 75.0 psi @Thickness 0.0620 in | Cured; ASTM D638 |
| Elongation at Break | 350 % @Thickness 1.57 mm | 350 % @Thickness 0.0620 in | Cured; ASTM D638 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.60e+14 ohm-cm | 1.60e+14 ohm-cm | Cured property; ASTM D257 |
| Dielectric Constant | 4.2 @Frequency 1000 Hz | 4.2 @Frequency 1000 Hz | Cured property; ASTM D150 |
| Dielectric Strength | 21.7 kV/mm @Thickness 0.127 mm | 550 kV/in @Thickness 0.00500 in | Cured; ASTM D149 |
| Dissipation Factor | 0.0030 @Frequency 1000 Hz | 0.0030 @Frequency 1000 Hz | Cured property; ASTM D150 |
| Thermal Properties | Metric | English | Comments |
| Thermal Conductivity | 1.00 - 2.00 W/m-K | 6.94 - 13.9 BTU-in/hr-ft²-°F | APTEK Test |