- 熔体流动速率 [g/10min]: 53.6
- 密度 [g/cm3]: 1.34
- 吸水率 [%]: 5.7
- 缺口冲击强度: 12.0
- 拉伸强度 [MPa]: 140.0
- 弯曲模量 [MPa]: 7.10
- 热变形温度 [℃]: 250.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.34 g/cc | 0.0484 lb/in³ | ISO 1183 | ||
| Water Absorption | 5.7 - 6.3 % | 5.7 - 6.3 % | ISO 62 | ||
| Moisture Absorption at Equilibrium | 1.2 - 1.6 % | 1.2 - 1.6 % | 23°C/50% R.H.; ISO 62 | ||
| Viscosity Test | 140 cm³/g | 140 cm³/g | Viscosity number; ISO 307 | ||
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | |||
| Melt Flow | 53.6 g/10 min @Load 5.00 kg, Temperature 275 °C | 53.6 g/10 min @Load 11.0 lb, Temperature 527 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 140 MPa | 20300 psi | 50mm/min; ISO 527 | ||
| Elongation at Yield | 3.0 % | 3.0 % | 50mm/min; ISO 527 | ||
| Modulus of Elasticity | 8.00 GPa | 1160 ksi | ISO 527 | ||
| Flexural Modulus | 7.10 GPa | 1030 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 12.0 kJ/m² | 5.71 ft-lb/in² | ISO 180/A | ||
| Charpy Impact Unnotched | 6.50 J/cm² | 30.9 ft-lb/in² | ISO 179/1eU | ||
| 6.00 J/cm² @Temperature -30.0 °C | 28.6 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 1.30 J/cm² | 6.19 ft-lb/in² | ISO 179/1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | IEC 60093 | ||
| Dielectric Constant | 3.7 @Frequency 1.00e+6 Hz | 3.7 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Dissipation Factor | 0.020 @Frequency 1.00e+6 Hz | 0.020 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Comparative Tracking Index | 550 V | 550 V | Test Solution A; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 25.0 - 35.0 µm/m-°C @Temperature 23.0 - 80.0 °C | 13.9 - 19.4 µin/in-°F @Temperature 73.4 - 176 °F | ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 60.0 - 80.0 µm/m-°C @Temperature 23.0 - 80.0 °C | 33.3 - 44.4 µin/in-°F @Temperature 73.4 - 176 °F | ISO 11359-1/-2 | ||
| Specific Heat Capacity | 1.50 J/g-°C | 0.359 BTU/lb-°F | |||
| Thermal Conductivity | 0.330 W/m-K | 2.29 BTU-in/hr-ft²-°F | DIN 52612 | ||
| Melting Point | 260 °C | 500 °F | DIN 53765 | ||
| Maximum Service Temperature, Air | 139 °C | 282 °F | for 50% loss of tensile strength after 20,000 hr | ||
| 157 °C | 315 °F | for 50% loss of tensile strength after 5,000 hr | |||
| 220 °C | 428 °F | ||||
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | ISO 75 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | ISO 75 | ||
| Flammability, UL94 | HB @Thickness >=0.400 mm | HB @Thickness >=0.0157 in | |||
| V-0 @Thickness >=0.800 mm | V-0 @Thickness >=0.0315 in | ||||
| 5VA @Thickness >=3.00 mm | 5VA @Thickness >=0.118 in | ||||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 280 - 300 °C | 536 - 572 °F | Injection-molding/Extrusion | ||
| Mold Temperature | 60.0 - 90.0 °C | 140 - 194 °F | Injection-molding | ||
| Descriptive Properties | |||||
| Color | Natural | ||||
| Commercial Status | North America and Europe | ||||
| Form | Pellets | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||
| Processing | Injection Molding | ||||
| Special characteristic | Flame retarding agent | ||||
| Heat stabilized or stable to heat | |||||
| Release agent | |||||