德国拜耳 PC 聚碳酸酯2258物性表
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.660 g/cc | 0.0238 lb/in³ | pellets; ISO 60 |
| Density | 1.20 g/cc | 0.0434 lb/in³ | ISO 1183-1 |
| Moisture Absorption at Equilibrium | 0.12 % | 0.12 % | ISO 62, 50% RH |
| Water Absorption at Saturation | 0.30 % | 0.30 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0065 cm/cm @Thickness 2.00 mm |
0.0065 in/in @Thickness 0.0787 in |
60x60x2 mm; 500 bar; ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0065 cm/cm @Thickness 2.00 mm |
0.0065 in/in @Thickness 0.0787 in |
60x60x2 mm; 500 bar; ISO 294-4 |
| Melt Flow | 37 g/10 min @Load 1.20 kg, Temperature 300 °C |
37 g/10 min @Load 2.65 lb, Temperature 572 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Puncture Resistance | 4900 N @Temperature 23.0 °C |
1100 lb (f) @Temperature 73.4 °F |
ISO 6603-2 |
| 5900 N @Temperature -30.0 °C |
1330 lb (f) @Temperature -22.0 °F |
ISO 6603-2 | |
| Ball Indentation Hardness | 115 MPa | 16700 psi | ISO 2039-1 |
| Tensile Strength at Break | 60.0 MPa | 8700 psi | 50 mm/min; ISO 527-1,-2 |
| Tensile Strength, Yield | 65.0 MPa | 9430 psi | 50 mm/min; ISO 527-1,-2 |
| Elongation at Break | >= 50 % | >= 50 % | Nominal, 50 mm/min; ISO 527-1,-2 |
| 125 % | 125 % | 50 mm/min; b.o. ISO 527-1,-2 | |
| Elongation at Yield | 6.0 % | 6.0 % | 50 mm/min; ISO 527-1,-2 |
| Tensile Modulus | 2.40 GPa | 348 ksi | 1 mm/min; ISO 527-1,-2 |
| Flexural Strength | 97.0 MPa | 14100 psi | 2 mm/min; ISO 178 |
| Flexural Yield Strength | 73.0 MPa @Strain 3.50 % |
10600 psi @Strain 3.50 % |
2 mm/min; ISO 178 |
| Flexural Modulus | 2.35 GPa | 341 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 12.0 kJ/m² @Thickness 3.20 mm, Temperature -30.0 °C |
5.71 ft-lb/in² @Thickness 0.126 in, Temperature -22.0 °F |
complete break; b.o. ISO 180-A |
| 65.0 kJ/m² @Thickness 3.20 mm, Temperature 23.0 °C |
30.9 ft-lb/in² @Thickness 0.126 in, Temperature 73.4 °F |
partial break; b.o. ISO 180-A | |
| Charpy Impact Unnotched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 179-1eU |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
ISO 179-1eU | |
| NB @Temperature -60.0 °C |
NB @Temperature -76.0 °F |
ISO 179-1eU | |
| Charpy Impact, Notched | 1.20 J/cm² @Thickness 3.00 mm, Temperature -30.0 °C |
5.71 ft-lb/in² @Thickness 0.118 in, Temperature -22.0 °F |
complete break; ISO 7391/b.o. ISO 179-1eA |
| 5.50 J/cm² @Thickness 3.00 mm, Temperature 23.0 °C |
26.2 ft-lb/in² @Thickness 0.118 in, Temperature 73.4 °F |
partial break; ISO 7391/b.o. ISO 179-1eA | |
| Puncture Energy | 55.0 J @Temperature 23.0 °C |
40.6 ft-lb @Temperature 73.4 °F |
ISO 6603-2 |
| 60.0 J @Temperature -30.0 °C |
44.3 ft-lb @Temperature -22.0 °F |
ISO 6603-2 | |
| Tensile Creep Modulus, 1 hour | 2100 MPa | 305000 psi | ISO 899-1 |
| Tensile Creep Modulus, 1000 hours | 1700 MPa | 247000 psi | ISO 899-1 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+16 ohm | 1.00e+16 ohm | IEC 60093 |
| Dielectric Constant | 3.0 @Frequency 1.00e+6 Hz |
3.0 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 3.1 @Frequency 100 Hz |
3.1 @Frequency 100 Hz |
IEC 60250 | |
| Dielectric Strength | 34.0 kV/mm @Thickness 1.00 mm |
864 kV/in @Thickness 0.0394 in |
IEC 60243-1 |
| Dissipation Factor | 0.00050 @Frequency 100 Hz |
0.00050 @Frequency 100 Hz |
IEC 60250 |
| 0.0090 @Frequency 1.00e+6 Hz |
0.0090 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 250 V | 250 V | Solution A; IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 65.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
36.1 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1,-2 |
| CTE, linear, Transverse to Flow | 65.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
36.1 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1,-2 |
| Thermal Conductivity | 0.200 W/m-K | 1.39 BTU-in/hr-ft²-°F | cross-flow; ISO 8302 |
| Hot Ball Pressure Test | 136 °C | 277 °F | IEC 60695-10-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 137 °C | 279 °F | ISO 75-1,-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 124 °C | 255 °F | ISO 75-1,-2 |
| Vicat Softening Point | 145 °C @Load 5.10 kg |
293 °F @Load 11.2 lb |
50°C/h; ISO 306 |
| 146 °C @Load 5.10 kg |
295 °F @Load 11.2 lb |
120°C/h; ISO 306 | |
| Glass Transition Temp, Tg | 145 °C | 293 °F | 10°C/min; ISO 11357-1,-2 |
| UL RTI, Electrical | 125 °C | 257 °F | UL 746B |
| UL RTI, Mechanical with Impact | 115 °C | 239 °F | UL 746B |
| UL RTI, Mechanical without Impact | 125 °C | 257 °F | UL 746B |
| Flammability, UL94 | HB @Thickness 2.90 mm |
HB @Thickness 0.114 in |
|
| V-2 @Thickness 0.750 mm |
V-2 @Thickness 0.0295 in |
||
| Flash Point | 480 °C | 896 °F | ASTM D 1929 |
| 550 °C | 1020 °F | self ignition; ASTM D 1929 | |
| Glow Wire Test | 875 °C @Thickness 0.750 mm |
1610 °F @Thickness 0.0295 in |
GWIT; IEC 60695-2-13 |
| 875 °C @Thickness 1.50 mm |
1610 °F @Thickness 0.0591 in |
GWIT; IEC 60695-2-13 | |
| 900 °C @Thickness 3.00 mm |
1650 °F @Thickness 0.118 in |
GWIT; IEC 60695-2-13 | |
| Optical Properties | Metric | English | Comments |
| Refractive Index | 1.586 | 1.586 | Procedure A; ISO 489 |
| Haze | <= 0.80 % @Thickness 3.00 mm |
<= 0.80 % @Thickness 0.118 in |
ISO 14782 |
| Transmission, Visible | 87 % @Thickness 4.00 mm |
87 % @Thickness 0.157 in |
ISO 13468-2 |
| 88 % @Thickness 3.00 mm |
88 % @Thickness 0.118 in |
ISO 13468-2 | |
| 89 % @Thickness 1.00 mm |
89 % @Thickness 0.0394 in |
ISO 13468-2 | |
| 89 % @Thickness 2.00 mm |
89 % @Thickness 0.0787 in |
ISO 13468-2 | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 280 °C | 536 °F | Injection molding; ISO 294 |
| Mold Temperature | 80.0 °C | 176 °F | Injection molding; ISO 294 |
| Injection Velocity | 200 mm/sec | 7.87 in/sec | ISO 294 |
•高韧性
•良好的耐热性
•玻璃般透明，光学质量
•高尺寸精度和稳定性
等级特点：
•医疗设备 - 生物相容性ISO10993-1
•低粘度;易释放
生产厂家：德国拜耳
生产型号 ： PC 聚碳酸酯2258
生产分类：聚合物;热塑性;聚碳酸酯（PC）;聚碳酸酯成型;聚碳酸酯，紫外线稳定
德国拜耳 PC 聚碳酸酯2258原材料内颗粒图：
德国拜耳 PC 聚碳酸酯2258原材料成型图咧：
德国拜耳 PC 聚碳酸酯2258塑料概括：
PC中文名：聚碳酸酯，英文名称为Polycarbonate，简称PC。是一种强韧的热塑性树脂，其聚碳酸酯是日常常见的一种材料。由于其无色透明和优异的抗冲击性，日常常见的应用有光碟，水瓶，眼镜片，防弹玻璃，护目镜、银行防子弹之玻璃、车头灯等等、动物笼子宠物笼子等。 偶尔也会应用到医疗器材或机械设备：各种齿轮、螺栓、曲轴、杠杆、轴承、齿条、凸轮、蜗轮蜗杆、、棘轮，也可作一些机械设备壳体、罩盖和框架等零件等等。
聚碳酸酯也是笔记本电脑外壳采用的材料的一种，它的原料是石油，经聚酯切片工厂加工后就成了聚酯切片颗粒物，再经塑料厂加工就成了成品，从实用的角度，其散热性能也比ABS塑料较好，热量分散比较均匀。
名称来源于其内部的CO3基团。可由双酚A和氧氯化碳（COCl2）合成。现较多使用的方法为熔融酯交换法（双酚A和碳酸二苯酯通过酯交换和缩聚反应合成）。制细菌特性、阻燃特性
聚碳酸酯还被用来制作登月太空人的头盔面罩。苹果公司的iPod音乐播放器和ibook笔记本电脑外壳也使用聚碳酸酯制作。
由于它的清晰和韧性，食物贮存货的生产者和采购员喜欢聚碳酸酯纤维。当与矽土玻璃比较聚碳酸酯纤维如同轻量级和高度不易碎。聚碳酸酯纤维多用于一次性塑料水瓶和重用塑料水瓶
德国拜耳 PC 聚碳酸酯2258性能：
绝缘性能：优良（潮湿、高温也能保持电性能稳定,是制造电子、电气零件的理想材料）；
机械性能：强度高、耐疲劳性、尺寸稳定、蠕变也小（高温条件下也极少有变化）；
德国拜耳 PC 聚碳酸酯2258物理特性
PC是一种非晶体工程材料，具有特别好的抗冲击强度、热稳定性、无色透明、抑制细菌特性、阻燃特性以及抗污染性。PC的缺口伊估德冲击强度（otched Izod impact stregth）非常高，并且收缩率很低，一般为0.1%~0.2%。
德国拜耳 PC 聚碳酸酯2258化学特性
PC塑胶原料它是一种新型的热塑性塑料，透明的度达90%，被誉为是透明金属。它刚硬而具有韧性，具有较高的冲击强度，高度的尺寸稳定性和范围很宽的使用温度、良好的电绝缘性能及耐热性和无毒性，可以通过注射、挤出成型。
PC有很好的机械特性，但流动特性较差，因此这种材料的注塑过程较困难。在选用何种品质的 PC材料时，要以产品的最终期望为基准。如果塑件要求有较高的抗冲击性，那么就使用低流动率的PC材料；反之，可以使用高流动率的PC材料，这样可以优化注塑过程。
德国拜耳 PC 聚碳酸酯2258成型条件与注意事项：
1．射出压力大，管内温度过高或滞留时间久时，易起热分解，变色及降低物性，须注意模温以85℃――120℃为准。
〔1〕水份控制在0.02%以下 〔2〕以120℃干燥4个小时，勿超过150℃
2．对厚的成品尤其不易成型，因成品易生残留应力，会造成日后破裂，因此宜用粉末状的硅利康作离模剂，勿用液状离模剂。
3．材料于使用前预作充分干燥。成型须高温及高压，须使用螺杆式成形梭。
4．浇口，流道设计应有较小的流动阻抗。
5．成型品设计应有近接之肉厚，避免有金属件镶嵌。再者，退缩倾斜须在2°以上。
6．加热温度230――310℃，模具80温度――120℃，料管温度260――310℃，喷出料温度280――320℃，射出压力800――1500kg/cm２,最低操作温度260℃。成型收缩率0.4――0.7%，比重1.2――1.5。