| 物性表： | |||||
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in³ | ISO 1183 | ||
| Water Absorption | 5.2 - 5.8 % | 5.2 - 5.8 % | ISO 62 | ||
| Moisture Absorption at Equilibrium | 1.5 - 1.9 % | 1.5 - 1.9 % | (23°C/50% R.H.); ISO 62 | ||
| Viscosity Test | 145 cm³/g | 145 cm³/g | Viscosity number; ISO 307 | ||
| Linear Mold Shrinkage | 0.0055 cm/cm | 0.0055 in/in | |||
| Melt Flow | 54.4 g/10 min @Load 5.00 kg, Temperature 275 °C |
54.4 g/10 min @Load 11.0 lb, Temperature 527 °F |
ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 130 MPa | 18900 psi | 50mm/min; ISO 527 | ||
| Elongation at Yield | 5.0 % | 5.0 % | 50mm/min; ISO 527 | ||
| Modulus of Elasticity | 7.20 GPa | 1040 ksi | ISO 527 | ||
| Flexural Strength | 210 MPa | 30500 psi | ISO 178 | ||
| Flexural Modulus | 6.50 GPa | 943 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 15.5 kJ/m² | 7.38 ft-lb/in² | ISO 180/A | ||
| Charpy Impact Unnotched | 10.0 J/cm² | 47.6 ft-lb/in² | ISO 179/1eU | ||
| Charpy Impact, Notched | 2.20 J/cm² | 10.5 ft-lb/in² | ISO 179/1eA | ||
| Tensile Creep Modulus, 1000 hours | 5300 MPa | 769000 psi | ISO 899 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+10 ohm-cm | 1.00e+10 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+10 ohm | 1.00e+10 ohm | IEC 60093 | ||
| Dielectric Constant | 5.6 @Frequency 1.00e+6 Hz |
5.6 @Frequency 1.00e+6 Hz |
IEC 60250 | ||
| Dissipation Factor | 0.16 @Frequency 1.00e+6 Hz |
0.16 @Frequency 1.00e+6 Hz |
IEC 60250 | ||
| Comparative Tracking Index | 550 V | 550 V | Test Solution A; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| Specific Heat Capacity | 1.50 J/g-°C | 0.359 BTU/lb-°F | |||
| Thermal Conductivity | 0.350 W/m-K | 2.43 BTU-in/hr-ft²-°F | DIN 52612 | ||
| Melting Point | 260 °C | 500 °F | DIN 53765 | ||
| Maximum Service Temperature, Air | 135 °C | 275 °F | for 50% loss of tensile strength after 20,000 hr | ||
| 165 °C | 329 °F | for 50% loss of tensile strength after 5,000 hr | |||
| 240 °C | 464 °F | ||||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 280 - 300 °C | 536 - 572 °F | |||
| Mold Temperature | 80.0 - 90.0 °C | 176 - 194 °F | |||
| De |
|||||
| Color | Natural | ||||
| Commercial Status | North America and Europe | ||||
| FDA | 21 CFR 177.1500 | ||||
| Form | Pellets | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||
| Processing | Injection Molding | ||||
| Special characteristic | Heat stabilized or stable to heat | ||||
上海松翰塑化科技有限公司，供应原料，品质真实,物实价廉。
PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。
欢迎各位客户前来咨询：
联系人： 夏先生
手 机：13501802636
QQ ：205730283
邮 箱 ：205730283@qq.com
导电尼龙66：具有良好的耐磨性、耐热性、耐油性及耐化学药品性，还大大降低了原材料的吸水率和收缩率,具有优良的尺寸稳定性及优异的机械强度。能满足静电消散和静电放电(ESD)防护的要求。这些特殊改性材料经特殊配制，适用于从100到1012欧姆/平方(ohms/sq)的表面电阻范围，可用于注塑及挤出等成型。有很多超越金属和涂装的优点:零件重量较轻，较易处理，运输成本较低。它们的装配简便，制造成本较低，并且较不会受到撞凹，割损和刮伤。为了标识或美观目的，一些材料可被预先染色，避免费时且昂贵的两次着色加工。
样图：