| 物性表： | |||||
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.12 g/cc | 0.0405 lb/in³ | dry; ISO 1183 | ||
| Water Absorption | 10.5 % | 10.5 % | beginning dry; ISO 62 | ||
| Moisture Absorption at Equilibrium | 3.2 % | 3.2 % | beginning dry (23°C/50% R.H.); ISO 62 | ||
| Relative Viscosity | 3.3 cP | 3.3 cP | ISO Test; 96 % SAV | ||
| Viscosity Test | 195 cm³/g | 195 cm³/g | Viscosity number | ||
| Linear Mold Shrinkage | 0.010 cm/cm | 0.010 in/in | ASTM Data; MD | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 45.0 MPa | 6530 psi | 50mm/min; ISO 527 | ||
| Elongation at Break | >= 50 % | >= 50 % | 50mm/min, Nominal strain; ISO 527 | ||
| Elongation at Yield | 20 % | 20 % | 50mm/min; ISO 527 | ||
| Tensile Modulus | 1.00 GPa | 145 ksi | 1mm/min; ISO 527 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 196 °C | 385 °F | 10 K/min | ||
| 196 °C | 385 °F | ASTM Test | |||
| De |
|||||
| Color | Natural | ||||
| Commercial Status | North America and Europe | ||||
| FDA | 21 CFR 177.1500 (restrictions per 21 CFR .1395) | ||||
| Form | Pellets | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Film Extrusion | ||||
| Processing | Other Extrusion | ||||
上海松翰塑化科技有限公司，供应原料，品质真实,物实价廉。
PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。
欢迎各位客户前来咨询：
联系人： 夏先生
手 机：13501802636
QQ ：205730283
邮 箱 ：205730283@qq.com
干燥处理：如果加工前材料是密封的，那么就没有必要干燥。然而，如果储存容器被打开，那么建议在85℃的热空气中干燥处理。如果湿度大于0.2%，还需要进行105℃，12小时的真空干燥。